Mechanical And Superconducting Properties Of Cu-Nb3Sn In Situ Produced Composite Wires

Published online by Cambridge University Press:  15 February 2011

A. Kolb-Telieps ,
B.L. Mordike  and
M. Mrowiec
A. Kolb-Telieps
Affiliation:
+Institut für Werkstoffkunde und Werkstofftechnik der Technischen Universität Clausthal
B.L. Mordike
Affiliation:
+Institut für Werkstoffkunde und Werkstofftechnik der Technischen Universität Clausthal
M. Mrowiec
Affiliation:
++Institut für Metallphysik, Universität Göttingen, West Germany
Get access

Abstract

Cu-Nb composite wires were produced from powder, electrolytically coated with tin and annealed to convert the Nb fibres to Nb 3Sn. The content was varied between 10 wt % and 40 wt %. The superconducting properties of the wires were determined. The mechanical properties, tensile strength, yield strength and ductility were measured as a function of volume fraction and deformation over a wide temperature range. The results are compared with those for wires produced by different techniques.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 12: Symposium L – In Situ Composites IV , 1981 , 277
Copyright
Copyright © Materials Research Society 1982

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Scanlan, R.M., Ann. Rev. Mater. Sci 10, 1980, p 113 CrossRefGoogle Scholar
2. Bormann, R., Schults, L., Freyhardt, H.C., Mordike, B.L., Zt. f. Metallkde 70, 1979, p 467 Google Scholar
3. Mrowiec, , diploma thesis, University Göttingen, 1981 Google Scholar
4. Wecker, , diploma thesis, University Göttingen, in preparationGoogle Scholar
5. Gregory, E., Marancik, W.G., Ormand, F.T., IEEE Trans. Mag., Vol. MAG-11, No. 2, 1975, p 295 Google Scholar
6. Harbison, J.P., Bevk, J., J. Appl. Phys. 48, 1977, p 5180 Google Scholar
7. Bevk, J. Harbison, J.P., Bell, J.L., J. Appl. Phys. 49, 1978, p 6031 Google Scholar
8. Frommeyer., G., Wassermann, G., acta met. 23, 1975, p 1353 CrossRefGoogle Scholar
9. Goudah, E., diploma thesis, Professorenstelle fur Werkstoffkunde, University Clausthal, 1979 Google Scholar
10. Hirsch, P.B., Trans JIM 9, 1968, p XXXX Google Scholar