Liquidus Temperature of Rare Earth-Alumino-Borosilicate Glasses for Treatment of Americium and Curium

Published online by Cambridge University Press:  10 February 2011

Brian J. Riley ,
John D. Vienna ,
Michael J. Schweiger ,
David K. Peeler  and
Irene A. Reamer
Brian J. Riley
Affiliation:
Pacific Northwest National Laboratory, Richlani, WA 99352
John D. Vienna
Affiliation:
Pacific Northwest National Laboratory, Richlani, WA 99352
Michael J. Schweiger
Affiliation:
Pacific Northwest National Laboratory, Richlani, WA 99352
David K. Peeler
Affiliation:
Westinghouse Savannah River Company, Aiken, SC 29808
Irene A. Reamer
Affiliation:
Westinghouse Savannah River Company, Aiken, SC 29808
Get access

Abstract

The liquidus temperatures, TL, of rare earth-alumino-borosilicate glasses were measured as a function of glass composition. The TL values ranged from 1153°C to 1405°C. Three primary crystalline phases were identified in the study. The most frequently encountered was a rare earth silicate phase in which the TL values ranged from 1153°C to 1405°C. A12O3 was encountered in glasses with an A12O3:SiO2 mass ratio greater than 1, with TL values ranging from 1242°C to 1305°C. Alumino-silicate crystals were encountered as the primary phase in glasses with less than 43 mass% of mixed rare earth oxides (Ln2O3) with TL values between 1164°C and 1255°C. A linear relationship between total mixed rare earth oxide concentration and TL was found within all three primary phase fields. In the rare earth silicate primary phase field, normalizing the Ln2O3 concentration with its mean ionic radius enhanced this linear relationship.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 608: Symposium QQ – Scientific Basis for Nuclear Waste Management XXIII , 1999 , 677
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1 Fellinger, A. P., Baich, M. A., Hardy, B. J., Jannik, G. T., Jones, T. M., Marra, J. E., Miller, C. B., Miller, D. H., Peeler, D. K., Synder, T. K., Stone, M. E., and Witt, D. C., Americium-Curium Vitrification Process Development, WSRC-MS-98-00864, Westinghouse Savannah River Company, Aiken, South Carolina (1998).Google Scholar
2 Peeler, D. K., Am-Cm: SrABS Glass Variability Study, Technical Task and QA Plan, WSRC-RP-98-01144, Rev. O, Westinghouse Savannah River Company, Aiken, South Carolina, (1998).Google Scholar
3 Peeler, D. K., and Edwards, T. B., Phase 2 Am/Cm Glass Variability Study, Technical Task and QA Plan. WSRC-RP-99-00272, Rev. O, Westinghouse Savannah River Company, Aiken, South Carolina, (1999).Google Scholar
4 Peeler, D. K., Edwards, T. B., Reamer, I. A., Vienna, J. D., Smith, D. E., Schweiger, M. J., Riley, B. J., and Crum, J. V., Composition/Property Relationships for the Phase 1 Am/Cm Glass Variability Study (U), WSRC-TR-99-00055, Westinghouse Savannah River Company, Aiken, South Carolina (1999).Google Scholar
5 Peeler, D. K., Edwards, T. B., Reamer, I. A.. Vienna, J. D., Smith, D. E., Schweiger, M. J., Riley, B. J., and Crum, J. V., “Composition/Property Relationships for the Phase 1 Am/Cm Glass Variability Study,” to be published (2000) in the Proceedings of the International Symposium on Waste Management Technologies in Ceramic and Nuclear Industries, Ceramic Transaction series.Google Scholar
6 Peeler, D.K., Edwards, T.B., Rudisill, T.S., Reamer, I.A, Vienna, J.D., Smith, D.E., Schweiger, M.J., and Riley, B.J. Composition /Property Relationships for the Phase 2 Am/Cm Glass Variability Study (U), WSRC-TR-99-00393, Rev. O, Westinhouse Savannah River Company, Aiken, South Carolina (1999b).Google Scholar
7 Vienna, J. D., Riley, B. J., Schweiger, M. J., Smith, D. E., Peeler, D. K., and Reamer, I. A., Property Data for Simulated Americium/Curium Glasses, PNNL- 13009, Pacific Northwest National Laboratory, Richland, Washington (1999).Google Scholar
8 Marra, J. E., Baich, M. A., Fellinger, A. P., Hardy, B. J., Jannik, G. T., Jones, T. M., Miller, C. B., Miller, D. H., Peeler, D. K., Synder, T. K., Stone, M. E., and Witt, D. C., “A Batch Process for Vitrification of Americium/Curium Solution (U),” to be published in the ACS proceedings (1999).Google Scholar
9 Shelby, J. E., and Kohli, J. T., “Rare-Earth Aluminosilicate Glasses,” J. Am. Ceram. Soc., 73 [1], 39–42, (1983).Google Scholar
10 Mika, M., Crum, J. V., and Hrma, P., “Spinel Precipitation In High-Level Waste Glass, in Proceedings of the 5th ESG Conference, Prague, Czech Republic, (1999).Google Scholar
11 Shannon, R. D., “Revised Effective Ionic Radii and Systematic Studies of Interatomic Distances in Halides and Chalcogenides,” in Acta Cryst. A32, 751–767, (1976).Google Scholar