Lattice Sites and Stability of Implanted Er in FZ and CZ Si

Published online by Cambridge University Press:  10 February 2011

U. Wahl ,
J. G. Correia ,
G. Langouche ,
A. Vantomme  and
Isolde collaboration
U. Wahl
Affiliation:
Instituut voor Kern- en Stralingsfysica, University of Leuven, Celestijnenlaan 200 D, B-3001 Leuven, Belgium, [email protected]
J. G. Correia
Affiliation:
CERN-PPE, CH-1211 Genève 23, Switzerland
G. Langouche
Affiliation:
Instituut voor Kern- en Stralingsfysica, University of Leuven, Celestijnenlaan 200 D, B-3001 Leuven, Belgium, [email protected]
A. Vantomme
Affiliation:
Instituut voor Kern- en Stralingsfysica, University of Leuven, Celestijnenlaan 200 D, B-3001 Leuven, Belgium, [email protected]
Isolde collaboration
Affiliation:
CERN-PPE, CH-1211 Genève 23, Switzerland
Get access

Abstract

We report on the lattice location of 167Er in Si measured by conversion electron emission channeling. In both FZ and CZ Si, a high fraction of Er (>65%) occupies near-tetrahedral interstitial (T) sites directly following 60 keV room temperature implantation at doses of 6× 1012 cm−2 For higher doses, the as-implanted near-T fractions of Er visible by emission channeling are smaller, due to the beginning of amorphization. Following the recovery of implantation damage at 600°C, more than 70% of Er is found on near-T sites in both FZ and CZ Si. In FZ Si, Er exhibits a remarkable thermal stability and only prolonged annealing for several hours reduces the near-T fraction. On the other hand, annealing of CZ Si at 900°C for more than 10 minutes results in the majority of Er probes in sites of very low symmetry or disordered surroundings.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 486: Symposium H – Materials & Devices for Silicon Based Optoelectronics , 1997 , 269
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Needels, M., SchlOter, M. and Lannoo, M., Phys. Rev. B 47, 15533 (1993).Google Scholar
[2] Gan, F., Assali, L.V.C. and Kimerling, L.C., Materials Science Forum, 196–201, 579 (1995).Google Scholar
[3] Ennen, H., Pomrenke, G., Axmann, A., Eisele, K., Haydl, W. and Schneider, J., Appl. Phys. Lett. 46, 381 (1985).Google Scholar
[4] Libertino, S., Coffa, S., Franzó, G. and Priolo, F., J. Appl. Phys. 78, 3867 (1995).Google Scholar
[5] Eaglesham, D.J., Michel, J., Fitzgerald, E.A., Jacobson, D.C., Poate, J.M., Benton, J.L., Polman, A., Xie, Y.H. and Kimerling, L.C., Appl. Phys. Lett. 58, 2797 (1991).Google Scholar
[6] Ren, F. Y. G., Michel, J., Sun-Paduano, Q., Zheng, B., Kitagawa, H., Jacobson, D. C., Poate, J. M. and Kimerling, L. C., Mat. Res. Soc. Proc. 301, 87 (1993).Google Scholar
[7] Przybylinska, H., Jantsch, W., Suprun-Belevitch, Y., Stephikhova, M., Palmetshofer, L., Hendorfer, G., Kozanecki, A., Wilson, R. J. and Sealy, B. J., Phys. Rev. B 54, 2532 (1996).Google Scholar
[8] Polman, A., J. Appl. Phys. 82, 1 (1997).Google Scholar
[9] Michel, J., Ren, F.Y.G., Zheng, B., Jacobson, D.C., Poate, J.M. and Kimerling, L.C., Materials Science Forum, 134–147, 707 (1994).Google Scholar
[10] Adler, D.L., Jacobson, D.C., Eaglesham, D.J., Marcus, M.A., Benton, J.L., Poate, J.M. and Citrin, P.H., Appl. Phys. Lett. 61, 2181 (1993).Google Scholar
[11] Terrasi, A., Franzo, G., Coffa, S., Priolo, F., D'Acapito, F. and Mobilio, S., Appl. Phys. Lett. 70, 1712 (1997).Google Scholar
[12] Nakashima, K., Eryu, O., hioka, O., Nakata, T. and Watanabe, M., Nucl. Instr. Meth. B 127, 475 (1997).Google Scholar
[13] Wahl, U., Vantomme, A., De Wachter, J., Moons, R., Langouche, G., Marques, J.G., Correia, J.G., and the ISOLDE collaboration, Phys. Rev. Lett. 79, 2069 (1997).Google Scholar
[14] Wahl, U., Correia, J.G., De Wachter, J., Langouche, G., Marques, J.G., Moons, R., Vantomme, A., and the ISOLDE collaboration, Mat. Res. Soc. Proc. 469 (1997) in print.Google Scholar
[15] Wahl, U., Correia, J.G., Langouche, G., Marques, J.G., Vantomme, A., and the ISOLDE collaboration, presented at the the International Conference on Defects in Semiconductors, Aveiro, 22.-25.7.97. See also CERN preprint PPE 97–139.Google Scholar
[16] Wahl, U., Correia, J.G., Cardoso, S., Marques, J.G., Vantomme, A., Langouche, G., and the ISOLDE collaboration, presented at the 13th International Conference on Ion Beam Analysis Lisbon, 27.7.-1.8.97, accepted for publication in Nucl. Instr. Meth. B.Google Scholar
[17] Weilhammer, P., Nygård, E., Dulinski, W., Czermak, A., Djama, F., Gadomski, S., Roe, S., Rudge, A., Schopper, F. and Strobel, J., Nucl. Instr. Meth. A 383, 89 (1996).Google Scholar