Ion Implantation-Induced Defects and the Influence of Titanium Silicidation

Published online by Cambridge University Press:  10 February 2011

D.Z. Chi ,
S. Ashok  and
D. Theodore
D.Z. Chi
Affiliation:
Dept. of Engineering Science, The Pennsylvania State University, University Park, PA 16802
S. Ashok
Affiliation:
Dept. of Engineering Science, The Pennsylvania State University, University Park, PA 16802
D. Theodore
Affiliation:
Motorola Inc., Mesa, AZ 852002
Get access

Abstract

Thermal evolution of ion implantation-induced defects and the influence of concurrent titanium silicidation in pre-amorphized p-type Si (implanted with 25 KeV, 1016 cm2Si+) under rapid thermal processing (RTP) have been investigated. Presence of implantation-induced electrically active defects has been confirmed by current-voltage (IV) and deep level transient spectroscopy (DLTS) measurements. DLTS characterization results show that the evolution of electrically active defects in the Si implanted samples under RTP depend critically on the RTP temperature: Hole traps HI (0.33 eV) and H4 (0.47 eV) appear after the highest temperature (950 °C) anneal, while a single trap H3 (0.26 eV) shows up at lower anneal temperatures (≤ 900 °C). The thermal signature of H4 defect is very similar to that of the iron interstitial while those of HI and H3 levels appear to originate from some interstitial-related defects, possibly complexes. A most interesting finding is that the above interstitial related defects can be eliminated completely with Ti silicidation, apparently a result of vacancy injection. However the silicidation process itself introduces a new H2 (0.30 eV) level, albeit at much lower concentration. This same H2 level is also seen in unimplanted samples under RTP. The paper will present details of defect evolution under various conditions of RTP for samples with and without the self-implantation and silicidation.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 510: Symposium D – Defect & Impurity Engineered Semiconductors & Devices II , January 1998 , 275
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Nocholas, K.H., J. Phys. D.9, 939 (1976)Google Scholar
2. Sze, S.M., VLSI Technology, MCGraw-Hill, New York, 1988 Google Scholar
3. Tsaur, B.Y. and Anderson, C.H. Jr., J. Apply. Phys., 54, 6336 (1983)Google Scholar
4. Raineri, V., Privitera, V., Galvagno, G., Priolo, F. and Rimini, E., Material Chemistry and Physics, 38, 105 (1994)Google Scholar
5. Jones, K.S., Prussin, S. and Weber, E., Apply. Physics. A 45, 1 (1988)Google Scholar
6. Ozturk, M.C., Frey, E., Chu, W.K. and Lee, C., IEEE Trans. Electron Devices ED-35, 659 (1988)Google Scholar
7. Stolk, P.A., Gossmann, H.J., Eaglesham, D.J. and Poate, J.M., Nucl. Instr. and Meth. B96, 187 (1995)Google Scholar
8. Wen, D.S., Smith, P.L., Osbum, C.M. and Rozgonyi, G.A., Appl. Phys. Lett., 51, 1182 (1987)Google Scholar
9. Kyllesbech Larsen, K., LaVia, F.. Lombardo, S. and Raineri, V., Appl. Phys. Lett., 67, 2931 (1995)Google Scholar
10. Brotherton, S.D., Gowers, J.P., Young, Y.D., Clegg, J.B. and Ayres, J.R., J. Appl. Phys., 60, 3567 (1986)Google Scholar
11. Papaioannou, G., Cristoloveana, S. and Hemment, P., J. Appl. Phys., 63, 4575 (1988)Google Scholar
12. , Rhoderick and , Williams, “Metal-Semiconductor Contacts”, CLARENDON PRESS, OXFORD, 1988 Google Scholar
13. Stolt, L. and Bohlin, K., Solid-state Electronics, Vol.28, No.12, 1215 (1985)Google Scholar
14. Barbier, D., Remram, M., Joly, J.F. and Laugier, A., J. Appl. Phys., 61, 156 (1987)Google Scholar
15. Jones, K.S. and Venables, D., J.Appl. Phys., 69, 2931 (1991)Google Scholar