Intrinsic Stress and Microstructural Evolution in Sputtered Nanometer Single and Multilayered Films

Published online by Cambridge University Press:  15 February 2011

Tai D. Nguyen
Tai D. Nguyen*
Affiliation:
Center for X-Ray Optics, Lawrence Berkeley Laboratory, University of California, Berkeley, CA 94720.
Get access

Abstract

The relationship of intrinsic stress and microstructural evolution in nanometer thick Mo and Si films, and Mo/Si multilayers deposited by magnetron sputtering at low working pressure (2.5 mTorr) is studied. The stress depends strongly on the microstructure which evolves with the film thickness. Transition from tensile to compressive films is observed in the metal films, in which nucleation and columnar grain growth occur. Deposition of layered Mo films by time-delayed sequential sputtering of thin layers results in smaller grains that do not extend through the film thickness, and in more tensile stress state than thick films of trie same thickness. The Si films are highly compressive at all thicknesses studied. The multilayers in this study show compressive stresses, with higher compressive stress at longer periods, and decreasing stress at shorter periods. The interface stress in amorphous Mo/Si multilayers is determined to be 1.1 J/m2. Comparison with values in other systems is made.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 343: Symposium H – Polycrystalline Thin Films - Structure, Texture, Properties and Applications , 1994 , 579
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Thornton, J.A., Tabock, J., and Hoffman, D.W., Thin Solid Films 64 (1979) 111.Google Scholar
2. Hoffman, D.W. and Thornton, J.A., J. Vac. Sci. Tech. 20, 3 (1982) 355.Google Scholar
3. Thornton, J.A., J. Vac. Sci. Tech. A4, 6 (1986) 3059.Google Scholar
4. Itoh, M., Hori, M., and Nadahara, S., J. Vac. Sci. Tech. B9, 1 (1991) 149.Google Scholar
5. Vink, T.J., Somers, M.A. J., Daams, J.L.C., and Dirks, A.G., J. Appl. Phys. 70, 8 (1991) 4301.Google Scholar
6. Pan, J.T. and Blech, I., J. Appl. Phys. 55 (1984) 2874.CrossRefGoogle Scholar
7. Stoney, G.G., Proc. Rov. Soc. Lon. A82 (1909) 72.Google Scholar
8. Brenner, A. and Sendroff, S., J. Res. Natl. Bur. Stand. 42 (1949) 105.Google Scholar
9. Davidenkov, N.N., Sov. Phys.-Solid State 2 (1961) 2595.Google Scholar
10. Timoshenko, S., J. Opt. Soc. Am. 11 (1925) 23.Google Scholar
11. Hoffman, R.W., Phys. Thin Films 3 (1966) 211.Google Scholar
12. Vilms, J. and Kerps, D., J. Appl. Phys. 53 (1982) 1536.CrossRefGoogle Scholar
13. Townsend, P.H., Barnett, D.M., and Brunner, T.A., J. Appl. Phys. 62 (1987) 4438.Google Scholar
14. Ruud, J.A., Witvrouw, A., and Spaepen, F., in Defects in Materials (MRS Proc. 209, 1991) 737.Google Scholar
15. Nguyen, T.D., Gronsky, R., and Kortright, J.B., J. Elec. Microsc. Tech. 19 (1991) 473.Google Scholar
16. Holloway, K., Do, K.B., and Sinclair, R., J. Appl. Phys. 65 (1989) 474.Google Scholar
17. Stearns, D.G., Stearns, M.B., Cheng, Y., Stith, J.H., and Ceglio, N.M., J. Appl. Phys. 67 (1990) 2415.Google Scholar
18. Nguyen, T.D., Lu, X., and Underwood, J.H., in Physics of X-Ray Multilayer Structures (OSA Tech. Digest Series 6, 1994) 102.Google Scholar
19. Nguyen, T.D., to be published.Google Scholar
20. Radelaar, S., in Advances in Phase Transitions, ed. by Embury, J.D. and Purdy, G.R. (Pergamon Press, Oxford, 1988) 178.Google Scholar
21. Nguyen, T.D., Ph.D. thesis, University of California at Berkeley (1993).Google Scholar