In-situ TEM Observation for Reaction Mechanism in MgH2 Hydrogen Storage Material

Published online by Cambridge University Press:  31 January 2011

Akifumi Ono ,
Shigehito Isobe ,
Yongming Wang ,
Naoyuki Hashimoto  and
Somei Ohnuki
Akifumi Ono
Affiliation:
[email protected]
Shigehito Isobe
Affiliation:
[email protected], Hokkaido University, Sapporo, Japan
Yongming Wang
Affiliation:
[email protected], Hokkaido University, Sapporo, Japan
Naoyuki Hashimoto
Affiliation:
[email protected], Hokkaido University, Sapporo, Japan
Somei Ohnuki
Affiliation:
[email protected], Hokkaido University, Sapporo, Japan
Get access

Abstract

In-situ observation on the catalytic effect of Nb2O5 in MgH2 was carried out by using transmission electron microscopy (TEM). We prepared two kinds of samples, because we tried to observe the reaction from two kinds of viewpoints. MgH2 catalyzed with 1 mol% of Nb2O5 was prepared for an overall viewpoint on the desorption process of MgH2 with catalyst by conventional TEM. The dehydrogenation of the 1 mol% sample started at 150 °C and Mg nano-size particles were formed. However, Nb2O5 was not confirmed in diffraction patterns and images, because it was highly dispersed by ball-milled. So MgH2 catalyzed with 10 mol% of Nb2O5 was prepared for local viewpoint to focus the boundary between the catalyst and the Mg phase by high voltage electron micro scope (HVEM). The sample mixed in mortar was prepared for this, because it was difficult to find the boundary in the sample ball-milled. The high resolution images of the 10 mol% sample revealed that the dehydrogenation started from the interface of MgH2 and Nb2O5. The result suggested that the dehydrogenation could proceed with hydrogen diffusion from MgH2 phase to the interface between Mg and Nb2O5.

Keywords

transmission electron microscopy (TEM)Mgcatalytic
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1216: Symposium W – Hydrogen Storage Materials , 2009 , 1216-W03-19
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Prigent, J. Gupta, M.: Journal of Alloys and Compounds 446-447 (2007) 90–95.Google Scholar
[2] Wang, X.L., Tu, J.P. Zhang, P.L. Zhang, X.B. Chen, C.P. Zha, X.B.: International Journal of Hydrogen Energy 32 (2007) 3406–3410 Google Scholar
[3] Schlapbach, L. Shaltiel, D. Oelhafen, P.: Materials Research Bulletin 14 (1979) 1235–1246 Google Scholar
[4] Barkhordarian, G. Klassen, T. Bormann, R.: Scripta Mater. 49 (2003) 213–217 Google Scholar
[5] Barkhordarian, G. Klassen, T. and Bormann, R.: Journal of Alloys and Compounds, 364 (2004) 242–246 Google Scholar
[6] Barkhordarian, G. Klassen, T. Bormann, R.: Journal of Alloys and Compounds, 407, (2006) 249–255 Google Scholar
[7] Hanada, N. Ichikawa, T. Fujii, H.: Journal of Alloys and Compounds, 404-406 (2005) 716–719 Google Scholar
[8] Hanada, N. Ichikawa, T. Hino, S. Fujii, H.: Journal of Alloys and Compounds, 420 (2006) 46–49 Google Scholar
[9] Hanada, N. Ichikawa, T. Fujii, H.: Physica B383 (2006) 49–50 Google Scholar
[10] Hanada, N. Hirotoshi, E. Ichikawa, T. Akiba, E. H, Fujii: Journal of Alloys and Compounds, 450 (2008) 395–399 Google Scholar
[11] Hanada, N. Ichikawa, T. Isobe, S. Nakagawa, T. Tokoyoda, K. Honma, T. Fujii, H. Kojima, Y.: J. Phys. Chem. C., 113, 13450 (2009).Google Scholar
[12] Porcu, M. Petford-Long, A.K., Sykes, J.M.: Journal of Alloys and Compounds 453 (2008) 341–346.Google Scholar