The Influence of Moisture on the Expansion of Macro-Defect-Free Cements

Published online by Cambridge University Press:  15 February 2011

H. Igarashi  and
T. Takahashi
H. Igarashi
Affiliation:
R&D Center of Cement Division Ube Industries, Ltd., Ube, Yamaguchi, Japan.
T. Takahashi
Affiliation:
R&D Center of Cement Division Ube Industries, Ltd., Ube, Yamaguchi, Japan.
Get access

Abstract

MDF(Macro-Defect-Free ) cement pastes, which consist of portland cement and polyvinyl alcohol/acetate, were prepared by varying the temperature during pressing and drying operations. We then examined the expansion of MDF cement pastes at various constant humidities. There was a large difference in expansion above 60%R.H. between samples prepared varying temperature at which samples were pressed. Samples pressed at 90 °C showed less expansion than samples pressed at 40 °C.

The pore structure of MDF cement pastes before exposure to moisture was measured by nitrogen adsorption, mercury intrusion porosimetry and image analysis. The properties of a matrix containing polyvinyl alcohol/acetate and cemnt hydrates were also investigated by TEM, IR and XPS.

There were not large differences in the result of IR and XPS measurement between the MDF cement pastes prepared at various temperatures. Calcium hydroxide crystal, lying perpendicular to cement particles, were often observed only in the MDF cement pastes pressed at 90 °C which occurs by water absorption, seems to be suppressed by calcium hydroxide crystal.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 245: Symposium K – Advanced Cementitious Systems: Mechanisms and Properties , 1991 , 173
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1 Birchall, J. D., Howard, A. J. and Kendall, K., Nature, 289 388(1981)10.1038/289388a0Google Scholar
2 Cannon, C. M. and Groves, G. W., J. Mater.Sci., 21 4009(1986)10.1007/PL00020273Google Scholar
3 Poon, C. S.,Wassell, L. E. and Groves, G. W., Mater.Sci.Technol., 3 993(1987)10.1179/mst.1987.3.12.993Google Scholar
4 Poon, C. S. and Groves, G. W., J. Mater.Sci., 23, 657(1988)10.1007/BF01174701Google Scholar
5 Yamaguchi, G. and Takagi, S., 5th Intern.Cong.Chem.Cem. (Tokyo), 1 181(1968)Google Scholar
6 McN.Alford, N., Birchall, J. D., Kendall, K. and Groves, G. W., J. Mater.Sci., 20, 3418(1985)10.1007/BF00545211Google Scholar
7 Groves, G. W., Cem.Concr.Res., 20, 315(1990)10.1016/0008-8846(90)90088-FGoogle Scholar
8 Rodger, S. A., Brooks, S. A., Sinclair, W., Groves, G. W. and Double, D. D., J. Mater. Sci., 20, 2853(1985)10.1007/BF00553048Google Scholar
9 Burkstrand, J. M., J. Appl.Phys., 52, 4795(1981)10.1063/1.329320CrossRefGoogle Scholar