High Modulus Liquid Crystalline Thermosetting Resins through Novel Processing Techniques

Published online by Cambridge University Press:  10 February 2011

M. E. Smith ,
E. P. Douglas ,
B. C. Benicewicz ,
J. D. Earls  and
R. D. Priester Jr
M. E. Smith
Affiliation:
Los Alamos National Laboratory, Polymers and Coatings Group, Los Alamos, NM 87545
E. P. Douglas
Affiliation:
Los Alamos National Laboratory, Polymers and Coatings Group, Los Alamos, NM 87545
B. C. Benicewicz
Affiliation:
Los Alamos National Laboratory, Polymers and Coatings Group, Los Alamos, NM 87545
J. D. Earls
Affiliation:
The Dow Chemical Company, Organic Product Research, Freeport, TX 77541
R. D. Priester Jr
Affiliation:
The Dow Chemical Company, Organic Product Research, Freeport, TX 77541
Get access

Abstract

We have demonstrated the effects of magnetic field alignment for the epoxy resin system, the diglycidyl ether of dihydroxy-α-methylstilbene cured with sulfanilamide. With increasing magnetic field, the tensile modulus of the thermoset can be enhanced by a factor of three, without compromise to the transverse value. Measurements of the coefficients of thermal expansion and the order parameter as determined by x-ray diffraction elucidate the high degree of alignment obtained at field strengths of 15–18 Tesla.

The interrelationship between the reaction kinetics of curing with the molecular alignment process is central to successful processing of this class of thermosets. Preliminary relationships between the field strength, time in the magnetic field, reaction rate, and extent of reaction have been developed. Process control and sequencing allow a wide adjustment in the properties of the produced samples. Our studies demonstrate the increased value of multi-mode processing in the development of tailored property, lightweight materials.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 425: Symposium I – Liquid Crystals for Advanced Technologies , 1996 , 167
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Moore, R.C., Denn, M.M. and Marrucci, G., Polym. Mater. Sci. Eng. 52, p. 84 (1985).Google Scholar
2. Maret, G. and Blumstein, A., Mol. Cryst. Liq. Cryst. 88, p. 295 (1982).Google Scholar
3. Lembicz, F., Polymer 32 p. 2898 (1991).Google Scholar
4. Moore, J.S. and Stupp, S.I., Macromolecules 20, p. 282 (1987).Google Scholar
5. Fuhrmann, K., Dries, Th., Fischer, E.W. and Ballauff, M., J. Polym. Sci., Part B: Polym. Phys. 30, p. 1199 (1992).Google Scholar
6. Barclay, G.G., McNamee, S.G., Ober, C.K., Papathomas, K.I. and Wang, D.W., J. Polym. Sci., Part A: Polym. Chem. 30, p. 1845 (1992).Google Scholar
7. Barclay, G.O., Ober, C.K., Papathomas, K.I. and Wang, D.W., Macromolecules 25, p. 2947, (1992).Google Scholar
8. Hoyle, C.E., Watanabe, T. and Whitehead, J.B., Macromolecules 27, p. 6581 (1994).Google Scholar
9. Humphreys, E.A. and Rosen, B. Walter, Engineered Materials Handbook. Vol. I Composites, ASM International, Metals Park, Ohio, 1987, p. 220.Google Scholar