High Deposition Rate P-I-N Solar Cells Prepared from Disilane Using VHF Discharges

H. Chatham; P. K. Bhat

doi:10.1557/PROC-149-447

Abstract

We report on the influence of the discharge excitation frequency on the material properties of intrinsic a-Si:H films deposited from disilane. A monotonic increase in the deposition rate with increasing frequency is observed in the range 13.56–110 MHz. Comparison of the properties of materials deposited at ˜1.5 nm/s using 13.56 and 110 MHz discharges in disilane indicates that there are some advantages to using 110 MHz. The performance of p-i-n devices fabricated from disilane at ˜2 nm/s at these two frequencies support this conclusion. We have fabricated a device from disilane at 1.8 nm/s using a frequency of 110 MHz with an AMl.5 efficiency of 9.7%.

References

REFERENCES

[1] Curtins, H., Wyrsch, N., Favre, M., and Shah, A.V., Plasma Chem. and Plasma Processing, 2, 267 (1987).Google Scholar

[2] Chatham, H. and Bhat, P.K., to be submitted to J. Appl. Phys.Google Scholar

[3] Freeman, E.C. and Paul, W., Phys, Rev. B. 18, 4288 (1978).Google Scholar

[4] Chatham, H. and Bhat, P.K., to be submitted to Appl. Phys. Lett.Google Scholar

[5] Flamm, D.L., J. Vac. Sci. Technol. A 4, 729 (1986).CrossRef Google Scholar

[6] Knights, J.C., Lujan, R.A., Rosenblum, M.R., Street, R.A., and Biegelsen, A.K., Appl. Phys. Lett 38, 331 (1981).Google Scholar

Crossref Citations

This article has been cited by the following publications. This list is generated based on data provided by Crossref.

Finger, F. Viret, V. Shah, A. Tang, X.-M. Weber, J. and Beyer, W. 1990. Hydrogen Incorporation in Amorphous Silicon Prepared at High Deposition Rates by the VHF-GD Technique. MRS Proceedings, Vol. 192, Issue. ,

Cho, G. Conti, M. Drewery, J.S. Fujieda, I. Kaplan, S.N. Perez-Mendez, V. Qureshi, S. and Street, R.A. 1990. Assessment of TFT amplifiers for a-Si:H PIXEL particle detectors. IEEE Transactions on Nuclear Science, Vol. 37, Issue. 3, p. 1142.

Finger, F. Kroll, U. Viret, V. Shah, A. Beyer, W. Tang, X. -M. Weber, J. Howling, A. and Hollenstein, Ch. 1992. Influences of a high excitation frequency (70 MHz) in the glow discharge technique on the process plasma and the properties of hydrogenated amorphous silicon. Journal of Applied Physics, Vol. 71, Issue. 11, p. 5665.

Zedlitz, Ralf Heintze, Moritz and Bauer, Gottfried H. 1992. Analysis of VHF Glow Discharge of A-SI:H Over a Wide Frequency Range. MRS Proceedings, Vol. 258, Issue. ,

Heintze, M Zedlitz, R and Bauer, G H 1993. Analysis of high-rate a-Si:H deposition in a VHF plasma. Journal of Physics D: Applied Physics, Vol. 26, Issue. 10, p. 1781.

Oda, S 1993. Frequency effects in processing plasmas of the VHF band. Plasma Sources Science and Technology, Vol. 2, Issue. 1, p. 26.

Perrin, Jérôme 1995. Plasma Deposition of Amorphous Silicon-Based Materials. p. 177.

Van Sark, W.G.J.H.M. Bezemer, J. Heller, E. M. B. Kars, M. and Van Der Weg, W. F. 1995. The Influence of Frequency and Pressure on the Material Quality of PECVD A-SI:H. MRS Proceedings, Vol. 377, Issue. ,

Pochet, T. Ilie, A. Brambilla, A. and Equer, B. 1996. Sensitivity measurements of thick amorphous-silicon p-i-n nuclear detectors. IEEE Transactions on Nuclear Science, Vol. 43, Issue. 3, p. 1452.

Heintze, M. 1997. Versatile High Rate Plasma Deposition and Processing with very high Frequency Excitation. MRS Proceedings, Vol. 467, Issue. ,

Stephan, U. Kuske, J. Frammelsberger, W. Lechner, P. Psyk, W. and Schade, H. 1997. Large area deposition technique for PECVD of amorphous silicon [solar cells]. p. 647.

Kuske, J. Stephan, U. Nowak, W. Röhlecke, S. and Kottwitz, A. 1997. Deposition Conditions for Large Area PECVD of Amorphous Silicon. MRS Proceedings, Vol. 467, Issue. ,

Jones, S.J. Deng, X. Liu, T. and Izu, M. 1999. Preparation of Triple-Junction A-Si:H NIP Based Solar Cells at Deposition Rates of 10 Å/s using a Very High Frequency Technique. MRS Proceedings, Vol. 557, Issue. ,

Jones, S.J. Williamson, D.L. Liu, T. Deng, X. and Izu, M. 2000. Comparison of Structural Properties and Solar Cell Performance of a-Si:H Films Prepared at Various Deposition Rates using 13.56 and 70 MHz PECVD Methods. MRS Proceedings, Vol. 609, Issue. ,

Jones, S.J. Liu, T. Deng, X. and Izu, M. 2000. a-Si:H-based triple-junction cells prepared at i-layer deposition rates of 10 a/s using a 70 MHz PECVD technique. p. 845.

Van Sark, Wilfried G.J.H.M. 2002. Advances in Plasma-Grown Hydrogenated Films. Vol. 30, Issue. , p. 1.

Ganguly, G. Carlson, D.E. and Arya, R.R. 2002. Effects of gas depletion on dc plasma deposited, a-Si single junction p–i–n solar cells with i-layers deposited at 10 Å/s. Journal of Non-Crystalline Solids, Vol. 299-302, Issue. , p. 1123.

Kumar, Sushil Dixit, P. N. Sarangi, D. and Bhattacharyya, R. 2003. High rate deposition of diamond like carbon films by very high frequency plasma enhanced chemical vapor deposition at 100 MHz. Journal of Applied Physics, Vol. 93, Issue. 10, p. 6361.

Ganguly, G Oswald, R.S and Carlson, D.E 2004. Optimization of the stabilized performance of amorphous silicon solar cells deposited at high growth rates by de-coupling of gas and superstrate temperatures. Applied Surface Science, Vol. 221, Issue. 1-4, p. 13.

Deb, Satyen K. 2004. Thin-Film Solar Cells. Vol. 13, Issue. , p. 15.

Download full list

Article contents

High Deposition Rate P-I-N Solar Cells Prepared from Disilane Using VHF Discharges

Abstract

Access options

References

REFERENCES

This article has been cited by the following publications. This list is generated based on data provided by Crossref.

Article contents

High Deposition Rate P-I-N Solar Cells Prepared from Disilane Using VHF Discharges

Abstract

Access options

References

REFERENCES

Save article to Kindle

Save article to Dropbox

Save article to Google Drive

Reply to: Submit a response

Your details

You have entered the maximum number of contributors

Conflicting interests