Growth Transients During the Nucleation of GaInAs on InP by Organometallic Vapor Phase Epitaxy

Published online by Cambridge University Press:  15 February 2011

D.T. Emerson  and
J.R. Shealy
D.T. Emerson
Affiliation:
OMVPE Facility, School of Electrical Engineering, Cornell University, Ithaca, NY 14850
J.R. Shealy
Affiliation:
OMVPE Facility, School of Electrical Engineering, Cornell University, Ithaca, NY 14850
Get access

Abstract

By using lattice matched short period (50 Å) GaInAs/InP superlattices, we are able to extensively characterize, ex-situ, nucleation of thin (20–30 Å) GaInAs layers on InP. Systematic variation of the interface formation technique allows us to understand how parameters such as growth temperature and growth rate can contribute to interfacial roughness, giving rise to growth transients near the interfaces that are unexpected from characterization of thick layers. Growth of multi-period structures such as those studied here enables the use of Raman scattering, photoluminescence, and double crystal x-ray diffraction to determine that Ga incorporation is favored over In incorporation near the InP to GaInAs interfaces. Furthermore, by examining the surfaces and structural properties of epitaxial layers (15 Å-1 μm) of both InP and GaInAs with atomic force microscopy and Raman scattering, respectively, we are able to correlate results on the superlattice structures with results from single layers. Finally, we show how understanding the nucleation of thin films through the process described here enables the growth of complicated, previously unrealizable, heterostructures for use in novel optoelectronic devices.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 440: Symposia CA – Structure and Evolution of Surfaces , 1996 , 169
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Wang, T.Y. and Stringfellow, G.B., J. Appl. Phys. 67, 344 (1990).Google Scholar
2. Landgren, G., Ojala, P., and Ekstrom, O., J. Crys. Growth 107, 573 (1991).Google Scholar
3. Clawson, A.R., Vu, T.T., Pappert, S.A., and Hanson, C.M., J. Crys. Growth 124, 536 (1992).Google Scholar
4. Bhat, R., Koza, M.A., Hwang, D.M., Kash, K., Caneau, C., and Nahory, R.E., J. Crys. Growth 110, 353 (1991).Google Scholar
5. Pitts, B.L., Matragrano, M.J., Emerson, D.T., Sun, B., Ast, D.T., and Shealy, J.R., Inst. Phys. Conf. Ser. 136 (IOP Bristol, 1993), 619.Google Scholar
6. Emerson, D.T., Whittingham, K.L., and Shealy, J.R., Inst. Phys. Conf. Ser. 141 (lOP Bristol, 1995), 155.Google Scholar
7. Emerson, D.T. and Shealy, J.R., Appl. Phys. Lett. 69, 383 (1996).Google Scholar
8. Emerson, D.T. and Shealy, J.R., Appl. Phys. Lett. 69, 2584 (1996).Google Scholar
9. Geurts, J., Gnoth, D., Finders, J., Kohl, A., and Heime, K., Phys. Stat. Sol. A 152, 211 (1995).Google Scholar
10. Clawson, A.R., Jiang, X., Yu, P.K.L., Hanson, C.M., and Vu, T.T., J. Elec. Mat. 22, 155 (1993).Google Scholar
11. Anan, T., Sugou, S., Nishi, K., and Ichihashi, T., Appl. Phys. Lett. 63, 1047 (1993).Google Scholar