Gallium Nitride Growth Using Diethylgallium Chloride as an Alternative Gallium Source

Published online by Cambridge University Press:  15 February 2011

Ling Zhang ,
Rong Zhang ,
Marek P. Boleslawski  and
T.F. Kuech
Ling Zhang
Affiliation:
Aldrich Chemical, Milwaukee, WI.
Rong Zhang
Affiliation:
Aldrich Chemical, Milwaukee, WI.
Marek P. Boleslawski
Affiliation:
Aldrich Chemical, Milwaukee, WI.
T.F. Kuech
Affiliation:
Aldrich Chemical, Milwaukee, WI.
Get access

Abstract

Metal organic vapor phase epitaxy (MOVPE) of GaN has been carried out using diethyl gallium chloride (DEGaCI) and ammonia. The growth rate and efficiency of the DEGaCl-based growth decreases with increasing temperature when compared to trimethyl gallium (TMG)-based growth under similar conditions. Both low temperature buffer and the high temperature GaN layers were grown using the DEGaCI-NH3 precursor combination on the basal plane of sapphire and compared to similar structures grown using TMG and NH3. DEGaCl-based growth reveals an improved growth behavior under identical growth conditions to the conventional TMGa and ammonia growth. X-ray, Hall, and atomic force microscopy (AFM) measurements have been carried out on these samples providing a direct comparison of materials properties associated with these growth precursors. For the DEGaCl-based growth, the x-ray rocking curve line width, using the (0002) reflection, is as low as 300 arcsec on a 2.5-micron thick film. A RMS surface roughness of ∼0.5nm measured over a 10x10 micron area.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 537: Symposium G – GaN and Related Alloys , 1998 , G3.62
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Morkoc, H., Strite, S., Gao, G. B., Lin, M. F., Sverdlov, B., and Burns, M., J. Appl. Phys. 76, 1363 (1994)Google Scholar
2 Nakamura, S., Fasol, G., The blue Laser Diode-GaN light Emitters and lasers (spring-Velag, Heidelberg, (1997).Google Scholar
3 Zhang, R. and Kuech, T.F., Appl. Phys. Lett. 72, 1611–1613 (1997).Google Scholar
4 Kuech, T. F., Potemski, R. and Cardone, F. J. Cryst. Growth V 124, 318–325 (1992)Google Scholar
5 Narmann, A., Yu, M.L. Surface Science V270, 1041–1047 (1992)Google Scholar
6 Kuech, T.F. J. Cryst. Growth V 115, 52–60 (1991)Google Scholar
7 Yamaguchi, Ko-ichi, Okamoto, K., Jpn. J. Appl. Phys. V32 4885–4888, (1993)Google Scholar
8 Shiraishi, y., Furuhata, N., Okamoto, A., J. Cryst. Growth V182, 255–265 (1997)Google Scholar
9 Buchan, N. I., Potemski, R. M., and Kuech, T. F., J. Chem. Engi. Data, V36, No. 4 (1991)Google Scholar
10 Stringfellow, G.B., Organometallic Vapor Phase Epitaxy, (Academic Press, San Diego, 1989) Chap. 3.Google Scholar
11 Look, D.C, Molnar, R.J., Appl. Phys. Lett. 70, 23 (1997).Google Scholar