Fiber Breakage In Polymer-Matrix Composites During Static And Fatigue Loading, Observed By Electrical Resistance Measurement

Published online by Cambridge University Press:  10 February 2011

Xiaojun Wang  and
D. D. L. Chung
Xiaojun Wang
Affiliation:
Composite Materials Research Laboratory, State University of New York at Buffalo Buffalo, NY 14260–4400
D. D. L. Chung
Affiliation:
Composite Materials Research Laboratory, State University of New York at Buffalo Buffalo, NY 14260–4400
Get access

Abstract

By measuring the electrical resistance of a continuous unidirectional carbon fiber epoxy-matrix composite along the fiber direction during loading in this direction, fiber breakage was progressively monitored in real time. Fiber breakage occurred in spurts involving 1000 fibers or more. It started at about half of the failure strain during static tensile loading and at about half of the fatigue life during tensiontension fatigue testing. Immediately before static failure, 35% of the fibers were broken. Immediately before fatigue failure, 18% of the fibers were broken. The fiber breakage was accompanied by decrease in modulus.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 503: Symposium JJ – Nondestructive Characterization of Materials in Aging Systems , 1997 , 81
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1. Muto, Norio, Yanagida, Hiroaki, Miyayama, Masaru, Nakatsuji, Teruyuki, Sugita, Minoru and Ohtsuka, Yasushi, J. Ceramic Soc. Japan 100 (4), 585 (1992).Google Scholar
2. Wang, X. and Chung, D.D.L., Smart Mater. Struct. 5, 796 (1996).Google Scholar
3. Wang, X. and Chung, D.D.L., Carbon 35, 706 (1997).Google Scholar