Failure of a Thermal Barrier System Due to a Cyclic Displacement Instability in the Thermally grown Oxide

Published online by Cambridge University Press:  17 March 2011

Daniel R. Mumm  and
Anthony G. Evans
Daniel R. Mumm
Affiliation:
Princeton Materials Institute, Princeton University Princeton, NJ 08540-5211, U.S.A., [email protected]
Anthony G. Evans
Affiliation:
Princeton Materials Institute, Princeton University Princeton, NJ 08540-5211, U.S.A.
Get access

Abstract

The mechanism controlling the cyclic failure of a commercial thermal barrier system has been investigated. The system comprises an electron-beam physical vapor deposited (EB-PVD) yttria-stabilized zirconia thermal barrier coating (TBC), deposited on a (Ni Pt) Al bond coating. The thermally grown oxide (TGO) layer that forms between the TBC and bond coat at high temperature is unstable with respect to out of plane displacement, provided initial perturbations are present. With cyclic thermal exposure, the TGO displaces into the bond coat at periodic interfacial sites. The out-of-plane displacements induce strains above the TGO, normal to the interface, that cause cracking. The cracks nucleate either within the TBC layer or at the TBC/TGO interface, and extend laterally until they coalesce with cracks from other sites and coating failure occurs by large scale buckling. The TGO displacements are accommodated by visco-plastic deformation of the underlying bond coat, and are driven by a lateral component of the growth strain in the TGO. The susceptibility of the TGO to out-of-plane displacement depends critically upon the initial morphology of the metal/oxide interface. The observed material responses are compared with predictions of a ‘ratcheting’ model.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 645: Symposium M – Thermal Barrier Coatings-2000 , 2000 , M2.6.1
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Miller, R.A., J. Am. Ceram. Soc., 67, 517 (1984).Google Scholar
2. Strangeman, T.E., Thin Solid Films, 127, 93 (1985).Google Scholar
3. Wright, P.K., Mat. Sci. Eng., A245, 191 (1998).Google Scholar
4. Stiger, M.J., Yanar, N.M., Toppings, M.G., Pettit, F.S. and Meier, G.H., Z. Metallk., 90, 1069 (1999).Google Scholar
5. DeMasi-Marcin, J.T. and Gupta, D.K., Surf. Coat. Tech., 68, 1 (1994).Google Scholar
6. Evans, A.G., Mumm, D.R., Hutchinson, J.W., Meier, G.H. and Pettit, F.S., Prog. Mater. Sci, (2000), in press.Google Scholar
7. Wright, P.K. and Evans, A.G., Curr. Op. Solid State Mater. Sci., 4, 255 (1999).Google Scholar
8. Sergo, V. and Clarke, D.R., J. Amer. Ceram. Soc., 81, 3237 (1998).Google Scholar
9. Tolpygo, V.K. and Clarke, D.R., Acta Mater., 48, 3282 (2000).Google Scholar
10. He, M.Y., Evans, A.G. and Hutchinson, J.W., Acta Mater., 48, 2593 (2000).Google Scholar
11. Choi, S.R., Hutchinson, J.W. and Evans, A.G., Mech. Mater., 31, 431 (1999).Google Scholar