Epitaxial LaNiO3Interlayers for Ferroelectric Memory Structures

Published online by Cambridge University Press:  15 February 2011

J. D. Klein ,
A. Yen  and
S. L. Clauson
J. D. Klein
Affiliation:
EIC Laboratories, Norwood, MA 02062
A. Yen
Affiliation:
EIC Laboratories, Norwood, MA 02062
S. L. Clauson
Affiliation:
EIC Laboratories, Norwood, MA 02062
Get access

Abstract

LaNiO3 thin films were utilized as metallic contact layers in ferroelectric capacitors. The LaNiO3 films were probably epitaxial when deposited atop (100) LaAlO3 substrates. They exhibited metallic resistivity over a wide range of temperature and oxygen partial pressure. Subsequent deposition of PZT and LaNiO3 thin films atop LaNiO3/LaAlO3 allowed realization of parallel-plate ferroelectric capacitor structures. The suitability of such devices for nonvolatile memory applications was surveyed through pulsed voltage testing. The observed 1-second remanent polarization exceeded 18 μC/cm2. Long-term memory was demonstrated for up to sixteen hours. No decrease in remanent polarization was apparent after more than 109 switching cycles.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 341: Symposium F – Epitaxial Oxide Thin Films and Heterostructures , 1994 , 393
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Ramesh, R., Chan, W.K., Wilkens, B., Sands, T., Tarascon, J.M., Keramidas, V.G., and Evans, J.T. Jr., Integrated Ferroelectrics 1, 1 (1992).Google Scholar
2. Eom, C.B., Marshall, A.F., Triscone, J.-M., Wilkens, B., Laderman, S.S., and Geballe, T.H., Science 251, 780 (1991).Google Scholar
3. Char, K., Colclough, M.S., Geballe, T.H., and Myers, K.E., Appl. Phys. Lett. 62, 196 (1993).Google Scholar
4. Wu, X.D., Foltyn, S.R., Dye, R.C., Coulter, Y., and Muenchausen, R.E., Appl. Phys. Lett. 62, 2434 (1993).CrossRefGoogle Scholar
5. Cheung, J.T., Morgan, P.E.D., Lowndes, D.H., Zheng, X.Y., and Breen, J., Appl. Phys. Lett. 62, 2045 (1993).Google Scholar
6. Satyalakshmi, K.M., Mallya, R.M., Ramanathan, K.V., Wu, X.D., Brainard, B., Gautier, D.C., Vasanthacharya, N.Y., and Hegde, M.S., Appl. Phys. Lett. 62, 1233 (1993).Google Scholar
7. Prasad, K.V.R., Varma, K.B., Raju, A.R., Satyalakshim, K.M., Mallya, R.M., and Hegde, M.S., Appl. Phys. Lett. 63, 1898 (1993).Google Scholar
8. Rajeev, K.P., Shivashankar, G.V., and Raychaudhuri, A.K., Solid State Commun. 79, 591 (1991).Google Scholar
9. Bernacki, S., Jack, L., Kisler, Y., Collins, S., Bernstein, S.D., Hallock, R., Armstrong, B., Shaw, J., Evans, J., Tuttle, B., Hammetter, B., Rogers, S., Nasby, B., Henderson, J., Benedetto, J., Moore, R., Pugh, R., and Fennelly, A., Integrated Ferroelectrics 3, 97 (1993).Google Scholar