Environmental and Stress State Effects on Fracture and Fatigue Crack-Growth in Zr-Ti-Ni-Cu-Be Bulk Amorphous Metals

Published online by Cambridge University Press:  10 February 2011

Katharine M. Flores ,
Daewoong Suh  and
Reinhold H. Dauskardt
Katharine M. Flores
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305
Daewoong Suh
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305
Reinhold H. Dauskardt
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305
Get access

Abstract

Our work has focused on the fracture and fatigue crack-growth mechanisms of a Zr41.25Ti13.75Ni10Cu12.5Be22.5 bulk metallic glass. These alloys exhibit failure strengths on the order of 2 GPa and toughnesses of 10–30 MPa√m with remarkably little plastic deformation. The effect of stress state on strength properties was studied in an effort to model fracture mechanisms. While fracture surfaces suggest significant plastic flow, failure strains are quite small and appear to be independent of stress state. Other methods of energy dissipation, including adiabatic heating, are discussed. Temperature increases of more than 20°C have been noted on the side face of the fracture sample at the crack tip during fracture. The micromechanics of fatigue crack growth are also considered and related to the batch chemistry, environment, and microstructure.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 554: Symposium MM – Bulk Metallic Glasses , 1998 , 355
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Bruck, H. A., Christman, T., Rosakis, A. J., and Johnson, W. L., Scripta Metall. 30, 429 (1994).Google Scholar
2. Conner, R. D., Rosakis, A. J., Johnson, W. L., and Owen, D. M., Scripta Metall. 37, 1373 (1997).Google Scholar
3. McClintock, in Fundamental Aspects of Structural Alloy Design, edited by Jaffee, R. I. and Wilcox, B. A. (Penum, New York, NY, 1977), p 147.Google Scholar
4. Mackenzie, A. C., Hancock, J. W., and Brown, D. K., Eng. Frac. Mech. 9, 167 (1977).Google Scholar
5. Spaepen, F., Acta Metall. 25, 407 (1911).Google Scholar
6. Bruck, H. A., Rosakis, A. J., and Johnson, W. L., J. Mater. Res. 11, 503 (1996).Google Scholar
7. Leonhard, A., Xing, L. Q., Heilmaier, M., Gerbert, A., Eckert, J., and Shultz, L., Nanostruct. Mater. 10 (1998), in press.Google Scholar
8. Kato, H. and Inoue, A., Mater. Trans. JIM 38, 793 (1997).Google Scholar
9. Doblione, R., Spriano, S., and Battezzati, L., Nanostruct. Mater. 8, 447 (1997).Google Scholar
10. Bengus, V. Z., Tabachnikova, E. D., Shumilin, S. E., Golovin, Y. I., Makarov, M. V., Shibokov, A. A., Miskuf, J., Csach, K., and Ocelik, V., Int, J. Rapid Solid. 8, 21 (1993).Google Scholar
11. Flores, K. M. and Dauskardt, R. H., J. Mater. Res. 14 (1999), in press.Google Scholar
12. Viswanadham, R. K., Green, J. A. S., and Montague, W. G., Scripta Metall. 10, 229 (1976).Google Scholar
13. Hancock, J. W. and Mackenzie, A. C., J. Mech. Phys. Solids 24,147 (1976).Google Scholar
14. Bridgman, P.W., Studies in Large Flow and Fracture, McGraw-Hill, New York (1952).Google Scholar
15. Rice, J. R. and Levy, N., in Physics of Strength and Plasticity, edited by Argon, A. S.(MIT Press, Cambridge, MA, 1969), p. 277.Google Scholar