Electromigration in Single-Crystal Aluminum Lines Pre-Damaged by Nanoindentation

Published online by Cambridge University Press:  15 February 2011

Young-Chang Joo ,
Shefford P. Baker ,
Michael P. Knaufß  and
Eduard Arzt
Young-Chang Joo
Affiliation:
Max-Planck-Institut fur Metallforschung and Institut for Metallkunde, University of Stuttgart, D-70174 Stuttgart, Germany
Shefford P. Baker
Affiliation:
Max-Planck-Institut fur Metallforschung and Institut for Metallkunde, University of Stuttgart, D-70174 Stuttgart, Germany
Michael P. Knaufß
Affiliation:
Max-Planck-Institut fur Metallforschung and Institut for Metallkunde, University of Stuttgart, D-70174 Stuttgart, Germany
Eduard Arzt
Affiliation:
Max-Planck-Institut fur Metallforschung and Institut for Metallkunde, University of Stuttgart, D-70174 Stuttgart, Germany
Get access

Abstract

Electromigration tests have been performed on single-crystal Al lines which were predamaged by rows of submicrometer-depth indentations made using a nanoindentation device. Indentations were placed close to each other so that their plastic deformation zones overlapped. During subsequent electromigration testing at 280°C and I to 2 MA/cm2, no damage was observed in non-indented single-crystal lines, while the indented lines showed electromigrationinduced voids at the cathode-side ends of the indented areas, and hillocks at the anode-side ends. The voids grew and moved away from the indentations towards the cathode. Fhe electromigration damage morphology of the indented lines indicates that the mechanical damage generates a local fast diffusion path in the single-crystal lines, which is believed to be due to dislocation core diffusion. A minimum indentation row length was observed, below which no void formed. This electromigration behavior is found to be phenomenologically similar to that of polygranular clusters in near-bamboo lines.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 428: Symposium L – Materials Reliability in Microelectronics VI , 1996 , 225
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Kinsbron, E., Appl. Phys. Lett. 36, 968 (1980).Google Scholar
2. Suo, Z., Acta Metall Mater. 42, 3581 (1994).Google Scholar
3. Baker, S. P., Knauss, M. P., Möckl, U. E., and Arzt, E., MRS Symp. Proc. 356, 483 (1995).Google Scholar
4. Joo, Y.-C., and Thompson, C. V., MRS Symp. Proc. 338, 319 (1994),Google Scholar
and Joo, Y.-C., Ph.D. Thesis, Massachusetts Institute of Technology, Cambridge, MA (1995).Google Scholar
5. Balluffi, R. W., Phys. Stat. Sol. 42, 11 (1970).Google Scholar
6. Arzt, E., Kraft, O., and Möckl, U. E., MRS Symp. Proc. 338, 397 (1994).Google Scholar
7. Arzt, E., and Nix, W. D., J. Mater. Res. 6, 731 (1991).Google Scholar
8. Blech, I., J. Appl. Phys. 47, 1203 (1976).Google Scholar
9. Schreiber, H. U., Solid State Electron. 28, 1153 (1985).Google Scholar