The Effects of Low Energy Ion-Beam Milling on the Physical and Electrical Properties of N-GaAs.

Published online by Cambridge University Press:  21 February 2011

W.F. Seng ,
P.A. Barnes ,
M.L. Lovejoy ,
L.P. Fu ,
G.D. Gilliland  and
D. Ila
W.F. Seng
Affiliation:
Department of Physics, Auburn University, AL 36849-5311 Department of Physics, Michigan Technological University, Houghton, MI
P.A. Barnes
Affiliation:
Department of Physics, Auburn University, AL 36849-5311
M.L. Lovejoy
Affiliation:
Department of Physics, Auburn University, AL 36849-5311
L.P. Fu
Affiliation:
Sandia National Laboratories, Albuquerque, NM 87185
G.D. Gilliland
Affiliation:
Department of Physics, Emory University, Atlanta, GA 30322
D. Ila
Affiliation:
Alabama A&M University, Center for Irradiation of Materials, Normal, AL 35762
Get access

Abstract

Low energy neutral Ar ion-beam etching of n-GaAs was investigated as a possible “cleaning” procedure prior to contact metallization. The ion-beam source energy was varied between 35 eV and 1200 eV at a fixed current density of 1 mA/cm2. The effects of ion-milling on lightly doped n-GaAs were analyzed electrically by measuring current-voltage (IV) and capacitance-voltage (CV) characteristics of Schottky barriers formed after the ion-milling. The metal semiconductor barriers were prepared immediately following ion-milling without breaking vacuum. Photoluminescence and Rutherford Backscattering (RBS) were used to determine if any physical modification of the surface and near surface region of the ion-milled substrates had occurred.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 396: Symposium A – Ion-Solid Interactions for Materials Modification and Processing , 1995 , 807
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Pang, S.W. and Piancentini, W.J., J. Vac. Sci. Technol., B1, 1334 (1983)Google Scholar
2 Kwan, P., Bhat, K.N., Borrego, J.M., Ghandi, S.K., Solid State Electron, 26, 125 (1983)Google Scholar
3 Cole, E.D., Sen, S., Burton, L.C., J. Electron. Materials, 18, 527, (1989)Google Scholar
4 Mellier-Smith, C.M., Mogab, C. J., Thin Film Processes. Edited by Vossen, J.L. and Kern, W. (Academic Press, New York, 1978), p 497.Google Scholar
5 Pearton, S.J., Chakrabarti, U.K., Perley, A.P., Jones, K.S., J. Appl. Phys., 68, 2760 (1990)Google Scholar