Effect of Polyvinylpyrrolidone Molecular Weight on the Critical Thickness, Crystallization, Densification and Properties of PLZT Films

Published online by Cambridge University Press:  01 February 2011

Zehui Du  and
J. Ma
Zehui Du
Affiliation:
[email protected], Nanyang Technological University, School of Materials Science and Engineering, Ceramics Lab,N4.1-B3-03, Nanyang Avenue,Nanyang Technological University, Singapore, Singapore, singapore, 639798, Singapore, 65-63168930, 65-67900920
J. Ma
Affiliation:
[email protected], Nanyang Technological Univerisity, School of Materials science and engineering, Ceramics lab,N4.1-B3-03,Nanyang Avenue, Singapore, Singapore, 639798, Singapore
Get access

Abstract

PLZT 9.5/65/35 ceramic films were prepared from the sol-gel solutions containing the stress-relaxing agent of polyvinylpyrrolidone(PVP) with the molecular weight of 40000, 360000 and 630000 (abbreviated as PVP40, PVP360 and PVP630) respectively. It is found that PVP40 can increase the critical thickness of the PLZT films to 0.22μm(compared with the critical thickness of 0.077μm in case of without PVP) and PVP360 and PVP630 can increase the critical thickness up to 0.49μm and 0.93μm individually. With the molecular weight of PVP increasing, the perovskite formation in the PLZT films was improved but the morphology of the films tended to be nano-porous. The films modified by PVP360 can be densified by optimizing the heat treatment conditions. When pyrolyzed at 600°C and then annealed at 700°C, the one-coating films with the thickness of 0.5μm were dense and exhibited a very slim hysteresis loop with the remnant polarization of 5.96×10−4μC/cm2 and coercive field of 21.51kV/cm, and a transmittance of around 90% and above in the wavelength of 450nm∼900nm.

Keywords

densificationphase transformationferroelectricity
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 928: Symposium GG – Current and Future Trends of Functional Oxide Films , 2006 , 0928-GG14-19
Copyright
Copyright © Materials Research Society 2006

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Nashimoto, K., Moriyama, H., Nakamura, S., et al, Opt. Fiber Commun.Conf., 4, PD10–1 (2001)Google Scholar
2. Glebov, Alexei L., Lee, Michael G., Huang, Lidu, et al., IEEE JOURNAL OF SELECTED TOPICS IN QUANTUM ELECTRONICS, 11, 422–430 (2005)Google Scholar
3. Jin, G. H., Zou, Y. K., Fuflyigin, V., et al., J. Lightwave Technology, 18, 807–812 (2000)Google Scholar
4. KOZUKA, H. et al, J. Sol-Gel Sci.Tech. 26, 681–686 (2003)Google Scholar
5. KOZUKA, H., Kajimura, M., et al, J. Sol-Gel Sci.Tech. 19, 205–209 (2000)Google Scholar
6. Kozuka, H., Takenaka, S., Tokita, H., et al, J. Euro.Ceram.Soc., 24, 1585–1588 (2004)Google Scholar
7. Kozuka, H., Takenaka, S., J. Am. Ceram. Soc., 85, 2696–702 (2002)Google Scholar
8. Takenaka, S., Kozuka, H., Appl.Phys.Lett., 79, 3485–3487 (2001)Google Scholar
9. Dogheche, E, Jaber, B., and Remiens, D., Appl.Opt., 37, pp.4245–4248 (1998)Google Scholar