Defects and Failure Modes in PZT Films for a MEMS Microengine

Published online by Cambridge University Press:  17 March 2011

D.F. Bahr ,
B.T. Crozier ,
C.D. Richards  and
R.F. Richards
D.F. Bahr
Affiliation:
Mechanical and Materials Engineering, Washington State University, Pullman, WA 99164-2920
B.T. Crozier
Affiliation:
Mechanical and Materials Engineering, Washington State University, Pullman, WA 99164-2920
C.D. Richards
Affiliation:
Mechanical and Materials Engineering, Washington State University, Pullman, WA 99164-2920
R.F. Richards
Affiliation:
Mechanical and Materials Engineering, Washington State University, Pullman, WA 99164-2920
Get access

Abstract

Piezoelectric films for a MEMS microengine have been deposited using solution deposition routines onto platinized silicon wafers. These films are used as membranes above a bulk micromachined cavity. A dynamic bulge tester and interferometer were used to characterize the deformation of the films when pressurized. The mechanical strain at failure, as well as the fatigue behavior, have been characterized. Membranes between 300 and 500 nm thick have been shown to sustain mechanical fatigue damage over approximately 10 million cycles at strains of 30% of the monotonic failure strain. Defects in the films due to growth and thermal stresses during processing, and their role in membrane failure, are identified. Crack growth is demonstrated in these films by compliance measurements during fatigue testing, and interfacial failure is identified between the PZT and Pt layers.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 657: Symposia EE – Materials Science of Microelectromechanical Systems (MEMS) Devices III , 2000 , EE4.4
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Fitzgerald, A.M., Dauskardt, R.H., and Kenny, T.W., Mat. Res. Soc. Symp. Proc., 605, 43 (2000).Google Scholar
2. Ballarini, R., Mat. Res. Soc. Symp. Proc., 546, 3 (1999).Google Scholar
3. Brown, S.B., Arsdell, W.V. Van, and Muhlstein, C.L., Transducers 97, 1997 International Conference on Solid-State Sensors and Actuators, p. 591 (1997).Google Scholar
4. Ding, X., Ko, W.H., and Mansour, J.H., Sensors and Actuators, A21–23, 866 (1990).Google Scholar
5. Bahr, D.F., Robach, J.S., Wright, J.S., Francis, L.F., and Gerberich, W.W, Mater. Sci. Eng. A, 259, 126 (1999).Google Scholar
6. Bahr, D.F., Merlino, J.C., Banerjee, P., Yip, C.M., and Bandyopadhyay, A., Mat. Res. Soc. Symp. Proc., 546, 153 (1999).Google Scholar
7. Cannon, R.M., Dalgleish, B.J., Dauskardt, R.H., Oh, T.S., and Ritchie, R.O., Acta Met.Mater., 39, 2145 (1991).Google Scholar
8. Kovacs, G.T.A., Micromachined Transducers, McGraw Hill, pp. 29–61 (1998).Google Scholar
9. Bahr, D.F., Crozier, B.T., Richards, C.D., and Richards, R.F., in Mechanical Properties of Structural Films, STP No. 1413, Muhlstein, C.L. and Brown, S.B., Eds., American Society for Testing and Materials, West Conshohocken, PA,(in press 2000).Google Scholar
10. Bonnotte, E., Delobelle, P., Bornier, L., Trolard, B., and , Tribillon, J. Mater. Res. 12, 2234 (1997).Google Scholar