Damage and Failure Mechanisms in High Pressure Silicon-Glass-Metal Microfluidic Connections

Published online by Cambridge University Press:  01 February 2011

Dong-Jin Shim ,
Hong-Wei Sun ,
Srikar T. Vengallatore  and
S. Mark Spearing
Dong-Jin Shim
Affiliation:
Department of Aeronautics and Astronautics, Massachusetts Institute of Technology, 77 Massachusetts Ave., Cambridge, MA 02139, USA
Hong-Wei Sun
Affiliation:
Department of Aeronautics and Astronautics, Massachusetts Institute of Technology, 77 Massachusetts Ave., Cambridge, MA 02139, USA
Srikar T. Vengallatore
Affiliation:
Department of Mechanical Engineering, McGill University, 817 Sherbrooke Street, W. Montreal, Quebec, Canada H3A 2K6
S. Mark Spearing
Affiliation:
Department of Aeronautics and Astronautics, Massachusetts Institute of Technology, 77 Massachusetts Ave., Cambridge, MA 02139, USA
Get access

Abstract

The characteristics and mechanisms of damage and failure in microfluidic joints consisting of Kovar metal tubes attached to silicon using borosilicate glass seals have been investigated. These joints are representative of seals for the MIT microrocket which is a silicon-based MEMS device. A key concern in such joints is the occurrence of cracks in silicon and glass due to residual stresses caused by a large thermal excursion during processing and the dissimilar coefficients of thermal expansion of the constituent materials. Joints with two types of glass compositions and joint configurations were fabricated, tested, and inspected. Axial tension tests were performed to investigate load carrying capability and the effect of thermally-induced cracks. Finite element models were used to obtain residual stresses due to the fabrication, and the location of the cracks from the experiments were found to coincide with the locations of the maximum principal stresses. The current work shows that the certain types of thermally-induced cracks are more detrimental to joint strength than others and a good bond between the Kovar tube and the silicon sidewall can help increase joint strength via shear load transfer.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 782: Symposium A – Micro- and Nanosystems , 2003 , A3.3
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Epstein, A. and Senturia, S.D., “Macro Power from Micro Machines”, Science, 276, 1211, 1997.Google Scholar
2. London, A.P., Ayon, A.A., Epstein, A., Spearing, S.M., Harrison, T., Peles, Y., and Kerrebrock, J.L., “Microfabrication of a high pressure bipropellant rocket engine”, Sensors and Actuators A, 92, 351–357, 2001.Google Scholar
3. Donald, I.W., “Preparation, properties and chemistry of glass and glass-ceramic-to-metal seals and coatings”, Journal of Materials Science, 28, 2841–2886, 1993.Google Scholar
4. Peles, Y., Srikar, V.T., Harrison, T., Protz, C., Mracek, A., and Spearing, S M., “Fluidic packaging of microengine and microrocket devices for high pressure and high temperature operation”, Journal of Microelectromechanical Systems, to appear Feb. 2004.Google Scholar