Chemical Vapor Deposition of Polycrystalline Silicon in a Rapid Thermal Processor

Published online by Cambridge University Press:  25 February 2011

Jimmy C. Liao ,
John L. Crowley  and
Ted I. Kamins
Jimmy C. Liao
Affiliation:
Peak Systems, Inc., Fremont, CA 94538
John L. Crowley
Affiliation:
Peak Systems, Inc., Fremont, CA 94538
Ted I. Kamins
Affiliation:
Hewlett-Packard, Palo Alto, CA 94303-0867
Get access

Abstract

The deposition of polycrystalline silicon in a rapid thermal processor was studied in the temperature range of 600-1100°C using a mixture of silane and argon at reduced pressures. The amorphous-to-polycrystalline transition temperature was determined by X-ray diffraction and UV-visible spectrophotometry to be between 650 and 700°C. The activation energy of the deposition was found to be approximately 1.5 eV in the temperature range of 600 to 800°C, in reasonable agreement with LPCVD and APCVD results. At 800°C and above, the deposition rate depended only weakly on temperature, as is characteristic of mass-transport-fimited processes. The partial pressure of silane was found to affect the deposition rate in both surface-limited and gas-transport-limited depositions. A UV-visible spectrophotometer was used as a reflectometer to measure the surface roughness of the samples, which in general increased with increasing deposition temperature and film thickness. At the lower deposition temperatures, the surfaces were very smooth, as is characteristic of amorphous-silicon films. Furthermore, the ability to change temperature rapidly appears to allow smoother films to be obtained by initially depositing at lower temperatures, and then ramping to a higher temperature to increase the deposition rate.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 146: Symposium B – Rapid Thermal Annealing/Chemical Vapor Deposition and Integrated Processing , 1989 , 97
Copyright
Copyright © Materials Research Society 1989

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Brown, W. A., Kamins, T. I., Solid State Technol, 22, (7), 51 (1979).CrossRefGoogle Scholar
2. Brekel, C. H. J. Van Den, Bollen, L. J. M., J. Crystal Growth, 54, 310 (1981).CrossRefGoogle Scholar
3. Foster, D., Learn, A., Kamins, T., Solid State Technol., 2–9, (5), 227 (1986).Google Scholar
4. Kamins, T. I., Polvcrystalline Silicon for Intesrated Circuit Applications. (Kluwer Academic Publishers, Norwell, MA 1988), p. 12.CrossRefGoogle Scholar
5. Gronet, C. M., Sturm, J. C., Williams, K. E., Gibbons, J. F. in Rarpid Thermal Processing, edited by Sedgwick, T. O., Seidel, T. E., Tsauer, B. (Mater. Res. Soc. Proc. 52, Pittsburgh, PA 1986) pp. 305–312.Google Scholar
6. Kamins, T. I., Mandurah, M. M., Saraswat, K. C., J. Electrochem. Soc., 126, 927, (1978).Google Scholar
7. Harbeke, G., Krausbauer, L., Steigemeier, E. F., Widmer, A. E., Kappert, H. F., Neugebauer, G., J. Electrochem, Soc., 131, 675, (1984).Google Scholar
8. Becker, F. S., Oppolzer, H., Weitzel, I., Eichermüller, H., Schaber, H., J. Appl. Phys., 56, 1233(1984).Google Scholar
9. Hatalis, M. K., Greve, D. W.. J. Appl. Phys., 63, 2260 1988.Google Scholar
10. Sturm, J. C., Gronet, C. M., Gibbons, J. F., IEEE Electron Dev. Lett., EDL–7, 282 1986.Google Scholar
11. Bravman, J. C., Patton, G. L., Plummer, J. D., J. Appl. Phys., 57, 2279 1985.Google Scholar
12. Harbeke, G., Meier, E., Sandercock, J. R., Tgetgel, M., Duffy, M. T., Soltis, R. A., RCA Rev., 44, 19 1983.Google Scholar
13. Chiang, K. L., Dell'Oca, C. J., Schwettmann, F. N., J. Electrochem. Soc., 126, 2267 1979.Google Scholar
14. Kamins, T. I., Polycrystalline Silicon for Integrated Circuit Applications, (Kluwer Academic Publishers, Norwell, MA 1988), p. 10.Google Scholar
15. Kamins, T. I., Polycrystalline Silicon for Integrated Circuit Applications, (Kluwer Academic Publishers, Norwell, MA 1988), p. 58.CrossRefGoogle Scholar
16. Nagasima, N., Kubota, N., Japan. J. Appl. Phys., 14, 1105 1975.Google Scholar
17. Kamins, T. I., J. Electrochem. Soc., 127, 686 1980.Google Scholar
18 Smith, J. V., editor, X-Ray Powder Data File (American Society for Testing and Materials, Philadelphia, PA 1960), Card 5-0565.Google Scholar
19. Cullity, B. D., Elements of X-ray Diffraction (Addison-Wesley publishers, Reading, MA 1956), p. 270, Eq. (9-4).Google Scholar