Characterization of Glassy State Relaxations in Styrene and Methacrylate Based Nonlinear Optical Materials

Published online by Cambridge University Press:  25 February 2011

Michael A. Schen
Affiliation:
National Institute of Standards and Technology, Polymers Division, Gaithersburg, MD 20899
Fred I. Mopsik
Affiliation:
National Institute of Standards and Technology, Polymers Division, Gaithersburg, MD 20899
Get access

Abstract

Sub-Ts relaxations in polymethylmethacrylate (PMMA) and in narrow molecular weight polystyrene (PS) thin films with and without second order nonlinear optical dyes have been examined using time domain dielectric spectrometry. Dyes used include 4-[N, N-dimethylamino]-4’-nitrostilbene (DANS) and 4-[N-ethyl, N-hydroxyethylaminoJ-4’-nitroazobenzene (DR1) at a level of 0.19 mole percent. In dye/PS blends, dye relaxations are seen to occur at frequencies similar to the frequencies of the β-relaxation of pure PS below the glass transition temperature. Analysis of the glassy phase dispersion leads us to conclude that, at near room temperature, appreciable dye reorientation occurs on a time scale of a few seconds. This dye reorientation is coupled to the dynamic motions of the localized polystyrene subunits. Experiments using dye in PMMA did not conclusively reveal dye motions because of the intrinsically large dispersion of PMMA itself. The β-relaxation frequency range is higher in the PMMA dye/polymer blend than in dye-containing PS implying dye reorientation would likewise occur more rapidly than in PS. Our results indicate that the randomization of dye orientation observed in a dye/polymer system depends on the rapid, local chain motions which continue at temperatures well below the glass transition temperature, as well as on the long range, slow relaxations associated with the glass-to-rubber transition.

Type
Research Article
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Hampsch, H.L., Yang, J., Wang, G.K., Torkelson, J.M., Macromolecules, 21, 526 (1988); 30 40 (1989); 23, 3640 (1990); 23, 3648 (1990);Google Scholar
Singer, K.D., Juzyk, M.G., Holland, W.R., Sohn, J.E., Lalama, S.J., Comizzoli, R.B., Katz, H.E., Schilling, M.L., Appl Phys. Leti., 53, 1800 (1988);Google Scholar
Singer, K.D., King, L. A., Polymer Preprints, 32(3), 98 (1991);Google Scholar
Dhinojwala, A.L., Wong, G.K., Torkelson, J.M., Polymer Preprints, 32 (3), 100 (1991).Google Scholar
2. Ferry, J.D., Viscoelastic Properties of Polymers, 2nd ed., John Wiley & Sons Publishers, New York, 1970.Google Scholar
3. McCrum, N.G., Read, B.E., Williams, G., Anelastic and Dielectric Effects in Polymeric Solids, Wiley & Sons Publishers, New York, 1967.Google Scholar
4. Sehen, M.A., Mopsik, F.I., Proc. of the SPIE, 1560, in press (1991).Google Scholar
5. Material suppliers, commercial equipment, or instruments are identified in this paper to adequately specify the experimental procedure. Such identification does not imply recommendation or endorsement by the National Institute of Standards and Technology or the United States Government.Google Scholar
6. Mopsik, F.I., Rev. Sci. Instrum., 55(1), 79 (1984).Google Scholar
7. a) Cole, R.H., Cole, K.S., J. Chem. Phys., 9 341 (1941);Google Scholar
b) McCrum, N.G., Read, B.E., Williams, G., Anelastic and Dielectric Effects in Polymeric Solids, pg. 116117, Wiley & Sons, New York, 1967.Google Scholar
8. Hampsch, H.L., Yang, J., Wong, G.K., Torkelson, J.M., Polymer Commun., 30, 40 (1989).Google Scholar
9. Hedvig, P., Dielectric Spectroscopv of Polymers, Wiley & Sons, New York, 1977, pg. 113119.Google Scholar