Capacitor Discharge Weld Modelling Using Ultra High Speed Photography

Published online by Cambridge University Press:  15 February 2011

R. D. Wilson ,
J. A. Hawk  and
J. H. Devletian
R. D. Wilson
Affiliation:
U.S. Bureau of Mines, Albany Research Center, Albany, Oregon 97321-2198
J. A. Hawk
Affiliation:
U.S. Bureau of Mines, Albany Research Center, Albany, Oregon 97321-2198
J. H. Devletian
Affiliation:
U.S. Bureau of Mines, Albany Research Center, Albany, Oregon 97321-2198
Get access

Abstract

Capacitor discharge welding (CDW) is a rapid solidification joining process where high cooling rates (106 K/s) are obtained as a result of the large weld surface area to small weld volume. The objective of this study, directed by the U.S. Bureau of Mines and the Oregon Graduate Institute of Science and Technology, was to use ultra-high speed photography to quantify transient arc behavior during the CDW cycle. The simple cylindrical geometries of the CD welds have been used to formulate analytical models which are compared to the high speed photographs of the welding process. The high speed photographs were analyzed with respect to welding time and process weld variables and compared to predicted values from the analytical model. The detailed photographic analyses revealed that material is continuously ejected as a plasma from the weld area due to induced magnetic forces, rather than having the liquid metal squeezed out of the weld upon contact. It was found that welding time was controlled by tip length and drop height. Results from high speed photographs found the arc travel speed around tube welds to be 109m/s. Finally, the high speed photographs revealed that the velocity of arc propagation during ignition was fast enough to allow the CDW process to be modelled as onedimensional heat flow.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 314: Symposium R – Joining and Adhesion of Advanced Inorganic Materials , 1993 , 151
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Wilson, R. D., Woodyard, J. R. Devletian, J. H., Weld. J. (suppl.) 72, 101s (1993).Google Scholar
2. Venkataraman, S. and Devletian, J. H., Weld. J. (suppl.) 67, 111s (1988).Google Scholar
3. Einerson, C. J., Clark, D. E. and Devletian, J. H., in Proc. of the 1987 ASME/JSME Thermal Engineering Joint Conf., Volume Three, edited by Marto, P. J. and Tanasawa, I.(ASME, New York, 1987), p. 217.Google Scholar
4. Wilson, R. D., PhD thesis, Oregon Graduate Institute of Science and Technology, 1991.Google Scholar
5. Burleigh, T. D. and Eagar, T. W., Metall. Trans A 14, 1223 (1983).CrossRefGoogle Scholar
6. Danks, D., MS thesis, Oregon Graduate Institute of Science and Technology, 1987.Google Scholar
7. Dogan, C. P., Wilson, R. D. and Hawk, J. A. in Joining of and Adhesion of Advanced Inorganic Materials, edited by Carim, A. H., Schwartz, D. S., Silberglitt, R. S. and Loehman, R. E. (Mater. Res. Soc. Proc., Pittsburgh, PA, 1993).Google Scholar