Behaviour of CS and I In Zirconia Based Fuel

Published online by Cambridge University Press:  15 February 2011

C. Degueldre
Affiliation:
Paul Scherrer Institute, CH-5232-Villigen-PSI, Switzerland
M. Pouchon
Affiliation:
Paul Scherrer Institute, CH-5232-Villigen-PSI, Switzerland
M. Doebli
Affiliation:
Paul Scherrer Institute, CH-5232-Villigen-PSI, Switzerland
G. Ledergerber
Affiliation:
Paul Scherrer Institute, CH-5232-Villigen-PSI, Switzerland
Get access

Abstract

A zirconia based ceramic is foreseen as an inert matrix fuel for burning excess plutonium in light water nuclear reactors. For reactor safety reasons the behaviour of volatile fission products such as cesium and iodine must be studied since a retention of fission products is favourable for licensing the studied inert matrix fuel. In this study, implantation of Cs and I was performed into polycrystalline (Zr0.85, Y0.15)O1.925 samples. The implantation depth was selected on the basis of the ability to observe by Rutherford backscattering spectroscopy (RBS) the behaviour of Cs and I after treatment. With a 1 MeV incident energy, the ions are implanted at a depth of 200 nm as predicted by TRIM. After implantations full quantification of I and Cs concentration profiles was performed by RBS. The implantation profiles are measured as a function of sample temperature during stepwise heating programs. It is interesting to observe retention of Cs and I at relatively high temperature (e.g. for 2 h, below 900 K for Cs and below 1400 K for I). This behaviour is likely to be due to the size and interactions of these species in the zirconia solid solution.

Type
Research Article
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Degueldre, C., Kasemeyer, U., Botta, F., Ledergerber, G., Mat. Res. Soc. Symp. Proc. 412, 15 (1996).Google Scholar
[2] Degueldre, C., Heimgartner, P., Ledergerber, G., Sasajima, N., Hojou, K., Muromura, T., Wang, L., Gong, W. and Ewing, R., Mat. Res. Soc. Symp. Proc. 439, 625 (1997).Google Scholar
[3] Pouchon, M.A., Dobeli, M., Degueldre, C., Nucl. Instr. and Meth. (in Press, 1999)Google Scholar
[4] Pouchon, M.A., Doebli, M.. Degueldre, C., Burghartz, M.. J. Nucl. Mater. Proc. 4th IMF workshop (submitted, 1999)Google Scholar
[5] Lambert, J.D.B. and Strain, R., in: Materials Science and Technology Vol 10A, ed. Frost, B.R.T. (VCH, 1994), p. 109.Google Scholar
[6] TRIM: http://www.research.ibm.com/ionbeams/SRIM/SRIMLEGL.HTMGoogle Scholar
[7] Borg, R. J., Dreucs, B. J., Solid state diffusion, Academic Press, Inc (1988)Google Scholar
[8] Accelerator: http://www.phys.ethz.ch/IPP/tandem/Welcome.htmlGoogle Scholar
[9] Chu, W.K., Mayer, J.W. and Nicolet, M.A.; Backscattering Spectrometry (Academic Press, 1978).Google Scholar
[10] Doolitle, L.R., Nucl. Instr. and Meth. B15 (1986) 227.Google Scholar
[11] Chevarier, N. et al. , Nucl. Instr. and Meth. in Phys. Res. B 136–138 (1998) 784.Google Scholar
[12] Perry, C., Feinberg, A., Solid State Commun. 36 (1980) 519522.Google Scholar
[13] Sakka, Y., Oishi, Y., Ando, K., Morita, S. J. Am. Ceram. Soc. 74 (1991) 2610–14.Google Scholar
[14] Periodic Table (Key data): http://www.shef.ac-uk/chemistry/web-elements/fr-key/Google Scholar
[15] Shannon, R., Prewitt, C., Acta Cryst. B25, 925 (1969).Google Scholar
[16] Degueldre, C., Takano, M., Ohmishi, T., Fukuda, K., Heimgartner, P., Graber, T., Energy transfer and thermal conductivity through inert matrix and nuclear analogous materials. JAERI research 97-087, Tokai-Mura, Ibaraki-ken, Japan, 1997 Google Scholar
[17] Thome, L. CNRS, Orsay (personal communication)Google Scholar