Application of Hot Wire Deposited Intrinsic Poly-Silicon Films in N-I-P cells and TFTS

Published online by Cambridge University Press:  15 February 2011

J. K. Rath ,
A.J.M.M. Van Zutphen ,
H. Meiling  and
R. E. I. Schropp
J. K. Rath
Affiliation:
Utrecht University, Debye Institute, P.O. Box 80000, 3508 TA Utrecht, The, Netherlands
A.J.M.M. Van Zutphen
Affiliation:
ECTM/DIMES-TU Delft, P.O. Box 5053, NL-2600 GB Delft, The, Netherlands
H. Meiling
Affiliation:
Utrecht University, Debye Institute, P.O. Box 80000, 3508 TA Utrecht, The, Netherlands
R. E. I. Schropp
Affiliation:
Utrecht University, Debye Institute, P.O. Box 80000, 3508 TA Utrecht, The, Netherlands
Get access

Abstract

Poly-silicon films have been prepared by hot-wire chemical vapour deposition (HWCVD) from hydrogen diluted silane gas at a low temperature (430 °C). The crystalline volume fraction is 95%. The grains have an average size of 70 nm and coalesce completely. The activation energy (0.54 eV) and the low carrier concentration (6.8 × 1010 cm−3) indicate the fully intrinsic nature of the films. The low (<1017 cm−3) defect density, the absence of 2100 cm−1 mode in infrared spectrum, the low activation energy of Hall mobility (0.012 eV) and the ambipolar diffusion length (LD) of 568 nm all indicate that the grain boundaries in the poly-Si:H films are indeed very thin. Preliminary n-i-p cells incorporating a poly-silicon i-layer yielded 3.15% efficiency and a current density of 18.2 mW/cm2 for only a 1.5 μm i-layer. In the solar cell, the conducting path is along the columnar grains ( (220) preferential orientation from XRD) and the carrier transport bypasses the grain boundary defects. This has been confirmed from the c-Si like optical absorption spectrum (measured by Dual Beam Photoconductivity in the cell configuration) at the low energy region. Inverted staggered thin-film transistors incorporating the poly-silicon layers showed transfer and output characteristics similar to those of state of the art a-Si:H TFTs : the saturation mobility is 0.4 cm2/Vs and the off current is approximately 10−11 A. This leads to the conclusion that the silicon near the SiO2 interface (the channel region) is still amorphous. This is illustrated by XTEM.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 467: Symposium A – Amorphous and Microcrystalline Silicon Technology - 1997 , 1997 , 445
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Rath, J.K., Ruff, D., Meiling, H. and Schropp, R.E.I., Proc. MRS Fall Meeting, Boston (1996) (in print).Google Scholar
2. Rath, J.K. et al, Tech. Digest Int. PVSEC-9, Miyazaki. Japan (1996) p227.Google Scholar
3. Rath, J.K., Meiling, H. and Schropp, R.E.I., Sol. Energy Mat. and Sol. Cells (in print).Google Scholar
4. Schropp, R.E.I., Feenstra, K.F., Molenbroek, E.C., Meiling, H. and Rath, J.K., Phil. Mag. B (in print).Google Scholar
5. Beck, N. et al, Proc. MRS Fall Meeting, Boston (1996) (in print).Google Scholar
6. Rath, J.K., Das, U.K. and Choudhuri, P., Proc. 13th EPVSEC, Nice (1995) p280.Google Scholar
7. St'ahel, P. and Sládek, P., Proc. 13th EPVSEC, Nice (1995) p214.Google Scholar
8. Choi, K. and Han, M., J. Appl. Phys. 80, 1883 (1996).Google Scholar
9. Meiling, H. and Schropp, R.E.I., Appl. Phys. Lett., (1997) (in print).Google Scholar
10. Doyle, R., Robertson, R., Lin, G.H., He, M.Z. and Gallagher, A., J. Appl. Phys. 64, 3215 (1988)Google Scholar
11. Rath, J.K. et al, Proc. 13th EPVSEC, Nice, (1995) p 1712.Google Scholar