Al-Doped ZnO Film as a Transparent Conductive Substrate in Indoline-Sensitized Nanoporous ZnO Solar Cell.

Published online by Cambridge University Press:  18 December 2012

B. Onwona-Agyeman ,
M. Nakao ,
G.R.A. Kumara  and
T. Kitaoka
B. Onwona-Agyeman
Affiliation:
Department of Agro-environmental Sciences, Graduate School of Bioresource and Bioenvironmental Sciences, Kyushu University, 6-10-1 Hakozaki, Higashi-ku, Fukuoka 812-8581, Japan
M. Nakao
Affiliation:
Department of Basic Science, Faculty of Engineering, Kyushu Institute of Technology, 1-1 Sensui, Tobata-ku, Kitakyushu 804-8550, Japan
G.R.A. Kumara
Affiliation:
Department of Chemistry, Peradeniya University, Peradeniya 20400, Sri Lanka
T. Kitaoka
Affiliation:
Department of Agro-environmental Sciences, Graduate School of Bioresource and Bioenvironmental Sciences, Kyushu University, 6-10-1 Hakozaki, Higashi-ku, Fukuoka 812-8581, Japan
Get access

Abstract

We have deposited porous ZnO films on aluminum-doped ZnO (ZnO/AZO) and fluorine-doped tin oxide (ZnO/FTO) transparent substrates, and annealed both in air at 500°C. X-ray diffraction measurements of the nanoporous ZnO films after heat treatment showed that, ZnO/AZO film exhibited a dominant (002) diffraction while the ZnO/FTO showed mixed diffraction peaks with the (100) and (101) being dominant. Dye-sensitized solar cells (DSC) based on the sensitization of the porous ZnO films on AZO and FTO substrates with an indoline dye were constructed. The photoaction spectrum, which is a measure of the degree of sunlight harvesting, was broad and higher in the ZnO/AZO DSC than that of the ZnO/FTO DSC. Conversion efficiency of 7.3 % was obtained for the ZnO/AZO DSC while 4.5 % was recorded for the ZnO/FTO. The superior photovoltaic performance of the ZnO/AZO DSC is attributed to better ZnO film orientation after thermal treatment and the higher sunlight harvesting.

Keywords

crystallographic structurephotovoltaictransparent conductor
Type
Articles
Information
MRS Online Proceedings Library (OPL) , Volume 1494: Symposium F – Oxide Semiconductors and Thin Films , 2013 , pp. 345 - 350
Copyright
Copyright © Materials Research Society 2012 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Grätzel, M., Nature 414, 338 (2001).CrossRefGoogle Scholar
Hagfeldt, A. and Grätzel, M., Chem. Rev. 95, 49 (1995).CrossRefGoogle Scholar
Grätzel, M., Curr. Opin. Colloid Interface Sci. 314 (1999).CrossRefGoogle Scholar
Kalyanasundaram, K. and Grätzel, M., Coord. Chem. Rev. 177, 347 (1998).CrossRefGoogle Scholar
Yan, S.G., Lyon, L.A., Lemon, B.I., Preiskorn, J.S. and Hupp, J.T., J. Chem. Educ. 74, 657 (1997).CrossRefGoogle Scholar
Birkholz, M., Selle, B., Fenske, F. and Fuhs, W., Phys. Rev. Lett. B 68, 205414 (2003).CrossRefGoogle Scholar
Major, S. and Chopra, K.L., Sol. Energy Mater. Sol. Cells, 17, 319 (1998).CrossRefGoogle Scholar
Horiuchi, T., Miura, H., Sumioka, K. and Uchida, S., J. Am. Chem. Soc. 126, 12218 (2004).CrossRefGoogle Scholar
Horiuchi, T., Miura, H. and Uchida, S., Chem. Commun. 3036 (2003).CrossRefGoogle Scholar
Ito, S., Miura, H., Uchida, S., Takata, M., Sumioka, K., Liska, P., Comte, P., Pechy, P. and Grätzel, M., Chem. Commun. 5194 (2008).CrossRefGoogle Scholar