Thermal Annealing Recovery and Saturation of Light-Induced Degradation of Amorphous Silicon Alloy Solar Cells with Different Microvoid Density

Published online by Cambridge University Press:  01 January 1993

X. Xu ,
J. Yang  and
S. Guha
X. Xu
Affiliation:
United Solar Systems Corp., 1100 W. Maple Rd., Troy, MI 48084
J. Yang
Affiliation:
United Solar Systems Corp., 1100 W. Maple Rd., Troy, MI 48084
S. Guha
Affiliation:
United Solar Systems Corp., 1100 W. Maple Rd., Troy, MI 48084
Get access

Abstract

We have studied the light-induced degradation and thermal annealing recovery of amorphous silicon alloy solar cells with different microvoid density in the intrinsic layer. The microvoid density was changed by altering the deposition rate. The experiments show that cells with higher microvoid density need longer annealing time to recover after prolonged light-soaking. As a consequence, cells with high density of microvoids do not seem to saturate even after long duration of light exposure. The cells with high microvoid density also show much lower degraded efficiency. A careful comparison between degradations caused by accelerated and one-sun light soaking and subsequent annealing recovery indicates that the defects created in the two cases have different nature.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 297: Symposium A – Amorphous Silicon Technology - 1993 , 1993 , 649
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Guha, S., Yang, J., Jones, S. J., Chen, Y., and Williamson, D. L., Appl. Phys. Lett. 61, 1444 (1992).Google Scholar
2. Guha, S., Final Report, SERI/TP-211-3918, the National Renewable Energy Laboratory, Golden, Colorado, 1990.Google Scholar
3. Park, H. P., Liu, J. Z., and Wagner, S., Appl. Phys. Lett. 55, 2658 (1989).Google Scholar
4. Banerjee, A., Guha, S., Pawlikiewcz, A., Wolf, D., and Yang, J., Amer. Inst. Phys. Conf. Proc. 234, 186 (1991).Google Scholar
5. Yang, L., Chen, L., and Catalano, A., p.259.Google Scholar
6. Stutzmann, M., Jackson, W. B., and Tsai, C. C., Phys. Rev. B32, 23 (1985).Google Scholar
7. Yang, L. and Chen, L., Private Communication.Google Scholar
8. Den Boer, W. and Guha, S., J. Appl. Phys. 57, 5539 (1985).Google Scholar
9. Stutzmann, M., Jackson, W. B., and Tsai, C. C., Phys. Rev. B34, 63 (1986).Google Scholar
10. Guha, S., Huang, C. Y., and Hudgens, S. J., Appl. Phys. Lett. 45, 50 (1984).Google Scholar
11. Crandall, R. S., Phys. Rev. Phys. Rev. B43, 4057 (1991).Google Scholar