Structure and Optical Characterization of Nanocrystalline Silicon Thin Films for Solar Cells

Published online by Cambridge University Press:  31 January 2011

Ryo Morisawa
Affiliation:
[email protected], Keio University, Yokohama, Japan
Akira Shirakura
Affiliation:
[email protected], Keio University, Yokohama, Japan
Chen-Chung Du
Affiliation:
[email protected], Industrial Technology Research Institute, Hsinchu, Taiwan, Province of China
Jen-Rong Huang
Affiliation:
[email protected], Industrial Technology Research Institute, Hsinchu, Taiwan, Province of China
Muh-Wang Liang
Affiliation:
[email protected], Industrial Technology Research Institute, Hsinchu, Taiwan, Province of China
David Ch Wu
Affiliation:
[email protected], Industrial Technology Research Institute, Hsinchu, United States
Tetsuya Suzuki
Affiliation:
[email protected], Keio University, Yokohama, Japan
Get access

Abstract

Effects of very high frequency- plasma enhanced chemical vapor deposition (VHF-PECVD) using diluted ultrapure silane at higher dilution ratio (R>30) on microstructures and optical characteristics of hydrogenated nanocrystalline silicon (nc-Si:H) film were studied. Nanocrystalline silicon films were prepared by at RF power ranging from 50 to 300 W. It was found that the transition from amorphous phase to nanocrystalline phase occurred between 100 W and 150 W. The nucleation mechanism toward nc-Si:H near the transition point of amorphous phase was discussed based on transmission electron microscopy with atomic scale. Further, it is suggested from UV-visible spectroscopy that nc-Si:H films with the best optical properties would be obtained near the transition point from the amorphous phase to the crystalline phase.

Type
Research Article
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Meier, J., Flückiger, R., Keppner, H. and Shah, A., Appl. Phys. Lett. 65 (1994) 860.Google Scholar
2 Kaneiwa, M, Nomoto, K. Progress in Photovoltaics: Research and Application, 10 (2002) 77.Google Scholar
3 Iqbal, Z. and Veprek, S., J. Phys. C 15 (1982) 377.Google Scholar
4 Matsuda, A., J. Non Non-Cryst. Solids 59&60 (1983) 767.Google Scholar
5 Tsu, R., Izu, M., Ovshinsky, S. R. and Pollak, F. H., Solid State C 36 (1980) 817.Google Scholar
6 Meier, J., Vallat-Sauvain, E. Vallat, Dubail, S., Kroll, U., Dubail, J. and Golay, S., Sol. Energy Mater. Sol. Cells 66 (2001) 73.Google Scholar
7 Rech, B., Roschek, T., Repmann, T., Müller, J., Schmitz, R. and Appenzeller, W., Thin Solid Films 427 (2003) 157.Google Scholar
8 Gutiérrez, M.T., Cárabe, J., Gandía, J.J. and Solonko, A., Sol. Energ. Mat. Sol. C. 26 (1992) 259.Google Scholar
9 Hine, R., Am. J. Phys. 33-11 (1965) 962.Google Scholar
10 Zhao, Z.X., Cui, R.Q., Meng, F.Y., Zhou, Z.B., Yu, H.C. and Sun, T.T., Solar Energy Mater. Sol. Cells 86 (2005) 135.Google Scholar
11 Smit, C., Swaaij, R. A. C. M. M. van, Petit, A. M. H. N., Kessels, W. M. M., and Sanden, M. C. M. van de, J. Appl. Phys. 94, (2003) 3582.Google Scholar
12 Ishihara, S., He, D., Shimizu, I., Jpn. J. Appl. Phys. 33 (1994) 51.Google Scholar