Structure and Mechanical Properties of Fe/Zr Multilayers.

Published online by Cambridge University Press:  22 February 2011

Joost J. Vlassak ,
Takenori Nakayama ,
Toyohiko J. Konno  and
William D. Nix
Joost J. Vlassak
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA. 94305
Takenori Nakayama
Affiliation:
Kobe Steel, Ltd., Japan
Toyohiko J. Konno
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA. 94305
William D. Nix
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA. 94305
Get access

Abstract

Iron zirconium multilayer films have been prepared by sputter deposition and studied using x-ray diffraction, high-resolution transmission electron microscopy and Nanoindenter techniques. The composition-modulation wavelength was varied between 0.8 and 92 nm. For modulation wavelengths greater than 4 nm the multilayers are crystalline with amorphous interfaces; for smaller wavelengths the samples are entirely amorphous. It was not possible to obtain layered structures with wavelengths smaller than 0.8 nm.

Both the hardness and the elastic modulus were measured as a function of composition-modulation wavelength by means of continuous indentation testing. The elastic modulus shows some variation with wavelength; the average value being 131 GPa. The hardness increases sharply when the modulation wavelength decreases below 4 nm. We attribute this increase to die crystalline to amorphous transition that occurs in these films at this wavelength.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 239: Symposium D – Thin Films: Stresses and Mechanical Properties III , 1991 , 493
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Kueny, A., Grimsditch, M., Miyano, K., Bannerjee, I., Falco, C.M. and Schuller, I.K., Phys. Rev. Lett. 48, 166 (1982)CrossRefGoogle Scholar
2. Khan, M.R., Chun, C.S.L., Felcher, G.P., Grimsditch, M., Kueny, A., Falco, C.M. and Schuller., I.K., Phys. Rev. B 27, 7186 (1983)Google Scholar
3. Zanoni, R., Bell, J.A., Stegeman, G.I. and Seaton, C.T., Thin Solid Films 154, 225 (1987)Google Scholar
4. Clemens, B.M. and Easley, G.L., Phys. Rev. Lett. 61, 2356 (1988)CrossRefGoogle Scholar
5. Lehoczky, S.L., Phys. Rev. Lett. 41, 1814 (1978)CrossRefGoogle Scholar
6. Lehoczky, S.L., J. Appl. Phys. 49, 5479 (1978)Google Scholar
7. Cammarata, R.C., Schlesinger, T.E., Kim, C., Qadri, S.B., Edelstein, A.S., Appl. Phys. Lett. 56, 1862 (1990)Google Scholar
8. Bunshah, R.F., Nimmagadda, R., Doerr, H.J., Movchan, B.A., Grechanuk, N.I. and Dabizha, E.V., Thin Solid Films 72, 261 (1980)Google Scholar
9. Bunshah, R.F., Nimmagadda, R., Doerr, H.J., Movchan, B.A., Grechanuk, N.I. and Dabizha, E.V., Thin Solid Films 112, 227 (1984)CrossRefGoogle Scholar
10. Cammarata, R.C. and Sieradzki, K., Phys. Rev. Lett. 62, 2005 (1989)Google Scholar
11. Koehler, J.S., Phys. Rev. B 2, 547 (1970)Google Scholar
12. Doermer, M.F., Nix, W.D., J. of Mater. Res. 1, 601 (1986)Google Scholar
13. Simmons, G. and Wong, H., ‘Single Crystal Elastic Constants and Calculated Aggregate Properties: a Handbook’, (MIT Press, Cambridge, 1971)Google Scholar
14. Clemens, B.M. and Gay, J.G., Phys. Rev. B: Rapid Comm. 35, 9337 (1987)CrossRefGoogle Scholar
15. Konno, T.J., Nakayama, T. and Sinclair, R., to be publishedGoogle Scholar
16. Clemens, B.M. and Suchoski, M.J., Appl. Phys. Lett. 47 (9), 943 (1985)Google Scholar
17. Krebs, H.U., Webb, D.J. and Marshall, A.F., Phys. Rev. B, 35, 5392 (1987)Google Scholar