Spinel Formation from Magnesium Aluminium Double Alkoxides

Published online by Cambridge University Press:  28 February 2011

Kenneth Jones
Affiliation:
Dept. of Chemistry University of Manchester Institute of Science and Technology, Manchester M60 1QD, England.
Thomas J. Davies
Affiliation:
Dept. of Metallurgy, University of Manchester Institute of Science and Technology, Manchester M60 1QD, England.
Harold G. Emblem
Affiliation:
Dept. of Chemistry University of Manchester Institute of Science and Technology, Manchester M60 1QD, England.
Peter Parkes
Affiliation:
Dept. of Chemistry University of Manchester Institute of Science and Technology, Manchester M60 1QD, England.
Get access

Abstract

Double alkoxides of the general formula Mg[Al(OR)4]2 where R is iso-Pr or sec-Bu were prepared by reacting aluminium and magnesium metals together with the alcohol ROH and purified by vacuum distillation. They were characterised by IR, proton and 27Al NMR spectroscopy and MW determination. A magnesium aluminium double alkoxide was also prepared by treating the commercially available aluminium alkoxide ‘Aliso B’ [a mixed aluminium (iso-propoxide)(sec-butoxide)] with magnesium and iso-propanol. Treatment of magnesium aluminium double alkoxides with water and an alkanolamine (preferably triethanolamine) gives a rigid coherent gel. Viscosity measurements and 27Al NMR spectroscopy suggest that the double alkoxide does not break down to its constituents during hydrolysis. The air-dried gel was shown by XRD to convert quantitatively to spinel on firing to 1500°C. The resistance of the double alkoxide moiety to hydrolysis explains the ease of conversion to spinel on firing. The gel has been used to bind alumina and magnesia grain. Gels suitable for binding refractory grain were obtained only when the alkanolamine content corresponded to one alkanolamine group per metal atom. Electron micrographic and XRD studies showed that in fired refractory pieces, the bonding phase was spinel.

Type
Articles
Copyright
Copyright © Materials Research Society 1986

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Moore, P.B. in McGraw-Hill Encylopedia of Science and Technology, 3rd ed. (McGraw-Hill Book Company, New York, 1982) Vol.12, pp. 903904.Google Scholar
2. Gilchrist, J.D., Fuels and Refractories. (Pergamon Press, Oxford, 1963) pp. 134135.Google Scholar
3. Meerwein, H. and Bersin, T., Ann. Chim. 476, 113 (1929).Google Scholar
4. Mehrotra, R.C., Goel, S., Goel, A.B., King, R.B. and Nainan, K.C., Inorg. Chim. Acta 29, 131 (1978).Google Scholar
5. Emblem, H.G., Jones, K. and Parkes, P., British Patent No. 2 128 604A (19 October 1982).Google Scholar
6. Parkes, P., PhD thesis, University of Manchester, 1984.Google Scholar
7. Emblem, H.G., Jones, K. and Parkes, P., European Patent Appliation No. 0 063 034 (7 April 1982).Google Scholar
8. Manchem Ltd., Ashton New Road, Manchester M11 4AT, UK; Data Sheet ‘Aliso and Aliso B’.Google Scholar
9. Heitler, C., Analyst 83, 223 (1958).CrossRefGoogle Scholar
10. ASTM PD File, Data Card 21–1152.Google Scholar
11. Derouane, E.G., Naggy, J.B., Gabelica, Z. and Blom, N., Zeolites 2, 229 (1983).Google Scholar