The Recrystallization Properties of Poly-GexSi1-xON SiO2/Si

Published online by Cambridge University Press:  10 February 2011

N. Jiang ,
J.R. Ma ,
M. Wu ,
X.D. Huang ,
S.L. Gu ,
S.D. Yu ,
L.Q. Hu  and
Y.D. Zheng
N. Jiang
Affiliation:
Department of Physics, Nanijing University, Nanjing, 210093, P.R. China, [email protected]
J.R. Ma
Affiliation:
Department of Physics, Nanijing University, Nanjing, 210093, P.R. China, [email protected]
M. Wu
Affiliation:
Department of Physics, Nanijing University, Nanjing, 210093, P.R. China, [email protected]
X.D. Huang
Affiliation:
Department of Physics, Nanijing University, Nanjing, 210093, P.R. China, [email protected]
S.L. Gu
Affiliation:
Department of Physics, Nanijing University, Nanjing, 210093, P.R. China, [email protected]
S.D. Yu
Affiliation:
Department of Physics, Nanijing University, Nanjing, 210093, P.R. China, [email protected]
L.Q. Hu
Affiliation:
Department of Physics, Nanijing University, Nanjing, 210093, P.R. China, [email protected]
Y.D. Zheng
Affiliation:
Department of Physics, Nanijing University, Nanjing, 210093, P.R. China, [email protected]
Get access

Abstract

In this paper, we have developed a new way to recrystallize the poly-GeSi on SiO2. 300nm poly-GeSi was grown by RTP/VLP-CVD on SiO2/Si, and then amorphized by 180 keV-Si+ ion implantation with dose of 2×10'4 cm'2. An amorphized region with the damage distribution was formed. After subsequent annealing process, the comparison between the XRD scans and Raman spectra of poly-GeSi and poly-Si indicated that the annealed poly-GeSi was more recrystallized than the poly-Si in the same conditions, this was the inducement of Ge in the annealing process. The segregation of Ge atoms in the heavy damaged region would enhance this inducement. The XTEM showed the longitudinal pattern of GeSi grains which meant the longitudinal sizes were much greater than the horizontal sizes. After annealing process, the final GeSi grain sizes were greater than the poly-Si grain sizes processed in SSIC with the same implantation conditions.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 472: Symposium I – Polycrystalline Thin Films - Structure, Texture, Properties..III , 1997 , 409
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Kwizera, P. and Reif, R. Appl. Phys. Lett. 41 (4) 379 (1982).Google Scholar
2. Wada, Yasuo and , ShigerNishimatsu J. Electrochem. Soc. Vol. 125 No. 9 1499 (1978).Google Scholar
3. Iverson, R.B. and Reif, R. J. Appl. Phys. 57(12) 5169 (1985).Google Scholar
4. Kung, K.T-Y. and Reif, R. J. Appl. Phys. 59(7) 2422 (1986).Google Scholar
5. Zheng, Youdou, Gu, Shulin, Han, Ping, Zhang, Rong and Hu, Liqun Progress in Physics (in Chinese) Vol. 13(1–2) 203 (1993).Google Scholar
6. Zheng, Youdou, Zhang, Rong, Hu, Liqun, Gu, Shulin, Wang, Ronghua and Han, Ping Mat. Res. Soc. Symp. Proc. Vol.263 227 (1992).Google Scholar
7. The Machanism and Technology of Ion Implantation (in Chinese), edited by Peking Radiant Center (Peking Press), p. 121.Google Scholar
8. Nayak, D.K., Kamjoo, K., Park, J.S., Woo, J.C.S., and Wang, K.L. Appl. Phys. Lett. 57 (4)369(1990).Google Scholar