PIEZORESPONSE FORCE MICROSCOPY STUDIES ON (100), (110) AND (111) EPITAXIALLY GROWTH BiFeO3 THIN FILMS

Published online by Cambridge University Press:  03 January 2013

R. P. Fernandes ,
L. Batista ,
A. C. G. Castro ,
L. Salamanca-Riba ,
M. P. Cruz ,
F. J. Espinoza-Beltrán ,
S. Hirsekorn ,
U. Rabe ,
J. Muñoz-Saldaña  and
G. A. Schneider
R. P. Fernandes
Affiliation:
Institute of Advanced Ceramics, Hamburg University of Technology, Denickstr. 15, 21073 Hamburg, Germany,
L. Batista
Affiliation:
Fraunhofer Institute for Nondestructive Testing (IZFP), Campus E3.1, 66123 Saarbrücken, Germany,
A. C. G. Castro
Affiliation:
Centro de Investigación y de Estudios Avanzados del I.P.N., Lib. Norponiente No. 2000, Fracc. Real de Juriquilla, C.P. 76230, Santiago de Querétaro, Qro., México,
L. Salamanca-Riba
Affiliation:
Materials Science and Engineering Department, University of Maryland, MD, USA
M. P. Cruz
Affiliation:
Universidad Nacional Autónoma de México, CNyN, Ensenada, B.C., México C.P. 22860
F. J. Espinoza-Beltrán
Affiliation:
Centro de Investigación y de Estudios Avanzados del I.P.N., Lib. Norponiente No. 2000, Fracc. Real de Juriquilla, C.P. 76230, Santiago de Querétaro, Qro., México,
S. Hirsekorn
Affiliation:
Fraunhofer Institute for Nondestructive Testing (IZFP), Campus E3.1, 66123 Saarbrücken, Germany,
U. Rabe
Affiliation:
Fraunhofer Institute for Nondestructive Testing (IZFP), Campus E3.1, 66123 Saarbrücken, Germany,
J. Muñoz-Saldaña
Affiliation:
Centro de Investigación y de Estudios Avanzados del I.P.N., Lib. Norponiente No. 2000, Fracc. Real de Juriquilla, C.P. 76230, Santiago de Querétaro, Qro., México,
G. A. Schneider
Affiliation:
Institute of Advanced Ceramics, Hamburg University of Technology, Denickstr. 15, 21073 Hamburg, Germany,
Get access

Abstract

Bismuth ferrite (BiFeO3) is a magnetoelectric, multiferroic material with coexisting ferroelectric and magnetic orderings. It is considered as a candidate for the next generation of ferroelectric random-access memory devices because BiFeO3, in contrast to industrial ferroelectrics used today, does not contain the toxic element lead. Furthermore, its polarization values are higher than those of lead-based ferroelectrics. The magnitude of the polarization of a BiFeO3 film is dependent on its orientation and is related to the domain structure. This contribution presents and discusses the preparation of epitaxial BiFeO3 (BFO) thin films grown on SrRuO3/SrTiO3 substrates by pulsed laser deposition (PLD) and their characterization, especially by piezo force microscopy (PFM) and atomic force acoustic microscopy (AFAM). The thickness of an individual BFO film varies between 100 and 200 nm. The epitaxial nature of films in the crystallographic (100), (110), and (111) directions was confirmed by x-ray diffraction (XRD). Thin SrRuO3 layers, also prepared by PLD, were used as bottom electrode for the ferroelectric hysteresis measurements. Low frequency PFM measurements showed a monodomain structure for the as-grown (110) and (111) oriented samples. In BFO (100) films, different polarization variants were observed by ultrasonic piezo force microscopy (UPFM). The domain structure is reproduced from minimization of the electrostatic and elastic energies. Switching experiments using standard PFM as well as UPFM were carried out on the three samples with the objective of testing the coercive field and domain stability. The AFAM technique was used to map the elastic properties of the BFO thin-films at the micro- and nanoscale.

Keywords

piezoresponselaser ablationBi
Type
Articles
Information
MRS Online Proceedings Library (OPL) , Volume 1477: Symposium S1A – Low-Dimensional Bismuth-based Materials , 2012 , imrc12-1477-s1a-o015
Copyright
Copyright © Materials Research Society 2012 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Hill, N.A., J. Phys. Chem. B 104: 6694–6709, (2000).10.1021/jp000114xCrossRefGoogle Scholar
Wang, J., Neaton, J. B., Zheng, H., et al. ., Science, 299: 1719, (2003).10.1126/science.1080615CrossRefGoogle Scholar
Catalan, G. and Scott, J. F., Adv. Mater. 21: 2463, (2009)10.1002/adma.200802849CrossRefGoogle Scholar
Ramesh, R, Spaldin, N.A., Nat. Mater. 6: 21–29, (2007).10.1038/nmat1805CrossRefGoogle Scholar
Singh, S.K, Ishiwara, H., Maruyama, K., J. Appl. Phys. 100: 64102–5, (2006).10.1063/1.2338836CrossRefGoogle Scholar
Chu, Y., Cruz, M.P., Yang, C., et al. ., Adv. Mater. 19: 2662–2666, (2007).10.1002/adma.200602972CrossRefGoogle Scholar
Chu, Y., Zhan, Q., Martin, L.W., et al. ., Adv. Mater. 18: 2307–2311, (2006).10.1002/adma.200601098CrossRefGoogle Scholar
Zhao, T., Scholl, A., Zavaliche, F., et al. . , Nat. Mater. 5: 823–829, (2006).10.1038/nmat1731CrossRefGoogle Scholar
Gruverman, A., Auciello, O., and Tokumoto, H., Annu. Rev. Mater. Sci. 28: 101 (1998)10.1146/annurev.matsci.28.1.101CrossRefGoogle Scholar
Rabe, U., Kopycinska, M., Hisekorn, S. et al. ., J. of Phys. D, 35: 2621, (2002).10.1088/0022-3727/35/20/323CrossRefGoogle Scholar
Rabe, U., Janser, K., and Arnold, W., Rev. Sci. Instrum. 67: 3281–3293, (1996).10.1063/1.1147409CrossRefGoogle Scholar
Zavaliche, F., Yang, S. Y., Zhao, T., et al. ., Phase Transitions. Phase Transitions 79: 991–1017, (2006).10.1080/01411590601067144CrossRefGoogle Scholar