The nucleation and growth of nano-structured diamond on phosphor and boron ions implanted Si substrates

Published online by Cambridge University Press:  11 February 2011

C. Z. Gu ,
L. Wei ,
Y. Sun ,
J. K. Jia  and
Z. S. Jin
C. Z. Gu
Affiliation:
State Key Laboratory for Surface Physics, Institute of Physics, 100080 Beijing, China
L. Wei
Affiliation:
State Key Laboratory for Surface Physics, Institute of Physics, 100080 Beijing, China
Y. Sun
Affiliation:
State Key Laboratory for Superhard Materials, Jilin University, 130023 Changchun, China
J. K. Jia
Affiliation:
State Key Laboratory for Superhard Materials, Jilin University, 130023 Changchun, China
Z. S. Jin
Affiliation:
State Key Laboratory for Superhard Materials, Jilin University, 130023 Changchun, China
Get access

Abstract

Nanocrystalline diamond films deposited by microwave plasma chemical vapor deposition (MWPCVD) method were observed on Si substrates implanted with phosphor (P) and boron (B) ions at room temperature via scanning electron microscopy (SEM). The relations between the species, energies and doses of implanted impurities and the nucleation, grain size and morphology of diamond were studied. The results present that different nucleation density from 106 cm-2 to 109 cm-2 can be obtained on implanted and unscratched Si, which is larger of 3–6 magnitude orders than that on mirror-polished Si. The nano-structured diamond films can be deposited on scratched Si substrates implanted by higher concentration of phosphor and boron ions. The grain sizes of nano-structured films can be adjusted by controlling the implanted energies and doses, and nano-structured films can be synthesized with low impressive stress. The Raman spectroscopy was employed to analysis the phase purity of nano-structured film, which shows a broad peak at around 1150 cm-1 relative to the nano-structured and tetrahedrally bonded carbon network.

Keywords

diamond nucleation and growthnano-structured filmion implantation
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 750: Symposium Y – Surface Engineering 2002–Synthesis, Characterization and Applications , 2002 , Y5.8
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Gruen, D.M., MRS Bulletin 9, 32(1998)Google Scholar
2. Schaller, E.M., Kuettel, O.M., Diederich, L., Schlapbach, L., Zhirnov, V.V., and Belobrov, P.I., Diamond Relat. Mater. 8, 805(1999)Google Scholar
3. Gu, C. Z., and Jiang, X., J. Appl. Phys. 88, 1788(2000)Google Scholar
4. Sharda, T., Soga, T., Jimbo, T., and Umeno, M., Appl. Phys. Lett., 80, 2880(2002)Google Scholar
5. Orwa, J. O., McCallum, J. C., Prawer, S., Nugent, K. W., Jamieson, D. N., Diamond and Related Materials, 8, 1642(1999)Google Scholar
6. Jiang, X., Schiffmann, K., and Klages, C.-P., Phys. Rev. B 50, 8402(1994)Google Scholar
7. Yabrough, W.A., and Messier, R., Science 247, 688(1990)Google Scholar