New Phenokena in Electron Beam Glazing

Published online by Cambridge University Press:  21 February 2011

P. R. Strutt ,
J. LeMAY  and
A. Tauqir
P. R. Strutt
Affiliation:
Metallurgy Department, University of Connecticut, Storrs, CT 06268
J. LeMAY
Affiliation:
Metallurgy Department, University of Connecticut, Storrs, CT 06268
A. Tauqir
Affiliation:
Metallurgy Department, University of Connecticut, Storrs, CT 06268
Get access

Abstract

Linear heat source surface melting studies have been carried out using a 1 to 15 kH oscillating beam incident on a steel substrate to produce a 3 to 35mm wide rapidly solidified strip of material at rates ranging from 1 to 100 cm.s−1. A simple relationship betweenmelt depth, power, and substrate velocity (V) has been determined at low values of V; limited results at higher velocities appear to follow the same relationship. A serendipitous discovery was the effect of prior surface homogenization treatment on the geometrical and microstructural uniformity of the subsequently formed rapidly solidified layers. This pre-treatment resulted in the formation of thin layers of uniform thickness under the most rapid processing condition (V = 100 cm.s−l). Omission of pre-treatnent resulted in irregular and sometimes discontinuous surface layers. In the case of a high speed steel of near peritectic composition (M2)pre-treatment resulted in the almost complete elimination of massive austenitic region within the dominant ferrite phase.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 28: Symposium F – Rapidly Solidified Metastable Materials , 1983 , 87
Copyright
Copyright © Materials Research Society 1984

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Breinen, E.M., Kear, B.H., Banas, C.M. and Greenwald, L.E., Superalloys- Metallurgy & Manufacture, Claitor, Baton Rouge, LA, 1976, p. 363.Google Scholar
2. Moore, P., Kim, C., Weinman, L.S., Laser-Solid Interaction & Laser Processing, Amer. Inst. Phys. Conf. Proc., 50, 221, (1979).Google Scholar
3. Copley, S.M., Beck, D., Esquivel, O., and Bass, M., Laser-Solid Interaction and Laser Processing, Amer. Inst. Phys. Conf. Proc., 50, 161 (1979).Google Scholar
4. Christodovlov, G., Henry, P., Steen, W.M., West, D.R.F., Rapidly Solidified Amorphous & Crystalline Alloys, Elsevier Sci. Publ. Inc., 1982, p. 505.Google Scholar
5. Mazumder, J. & Steen, W.M., J. Appl. Phys., 51, 941, (1980).10.1063/1.327672Google Scholar
6. Lewis, B.G. & Strutt, P.R., J. of Metals, p. 37, (1982).10.1007/BF03338137Google Scholar
7. Strutt, P.R., Kurup, M. & Taquir, A., Proc. N.B.S. Conf. on Rapid Solidification Gaithersburg 1983.Google Scholar
8. Hashimoto, T. & Matsuda, F., Trans. Nat. Rev. Inst. Miet., 7, 96, (1965).Google Scholar
9. Strutt, P.R., Mat. Sci. & Engr., 44, 239 (1980).10.1016/0025-5416(80)90124-XGoogle Scholar
10. Block, M.J., Nature, 178, 650, (1956).10.1038/178650a0Google Scholar
11. Nield, D.A., J. Fluid Mlech., 29, 545, (1967).10.1017/S0022112067001028Google Scholar