Microscale Fracture Testing of Mg-Zn-Y

Published online by Cambridge University Press:  31 January 2011

Shun Matsuyama ,
Tetsuya Sakamoto ,
Masaaki Otsu ,
Kazuki Takashima  and
Yoshihito Kawamura
Shun Matsuyama
Affiliation:
[email protected], Kumamoto University, Materials Science & Engineering, Kumamoto, Japan
Tetsuya Sakamoto
Affiliation:
[email protected], Kumamoto University, Materials Science & Engineering, Kumamoto, Japan
Masaaki Otsu
Affiliation:
[email protected], Kumamoto University, Materials Science & Engineering, Kumamoto, Japan
Kazuki Takashima
Affiliation:
[email protected], Kumamoto University, Materials Science & Engineering, 2-39-1 Kurokami, Kumamoto, 860-8555, Japan, +81-96-342-3716, +81-96-342-3716
Yoshihito Kawamura
Affiliation:
[email protected], Kumamoto University, Kurokami, Japan
Get access

Abstract

A microfracture testing technique was applied for investigating the fracture properties of Mg-Zn-Y alloys with a long-period stacking ordered (LPSO) phase. Microsized cantilever beam specimens with dimensions ≈ 10×20×50 μm3 were prepared from Mg-Zn-Y alloys by focused ion beam (FIB) machining. Notches with widths of 0.5 μm and depths of 3.5–5 μm were also introduced into the specimens by FIB machining. In this study, three types of Mg-Zn-Y alloys―Mg99.2Zn0.2Y0.6, Mg97Zn1Y2, and Mg88Zn5Y7―were used. Fracture tests were successfully conducted using a mechanical testing machine for microsized specimens at room temperature. The fracture toughness values (KIC) could not be obtained as the specimen size was too small to satisfy the plane strain condition. Hence, provisional KQ values were considered. The KQ values of the Mg97Zn1Y2 alloy were 0.8–1.2 MPam½, and those of the Mg88Zn5Y7 alloy were 1.2–3.0 MPam½. As the fracture in the Mg99.2Zn0.2Y0.6 alloy specimen occurred in a ductile plastic deformation, it was impossible to evaluate KQ values of this specimen. The increasing volume fraction of the LPSO phase indicates that the fracture toughness of Mg-Zn-Y alloys increases in LPSO phase.

Keywords

Mgfracturesecond phases
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1225: Symposium HH – Multiscale Polycrystal Mechanics of Complex Microstructures , 2009 , 1225-HH03-04
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Kawamura, Y. Yamasaki, M. Materials Transactions 42, 1172 (2001)Google Scholar
2 Itoi, T. Semiya, T. Kawamura, Y. Hirohashi, M. Scripta Materialia 56, 543 (2006).Google Scholar
3 Gerado, G. Maria, M. Iain, T. Pablo, P. Paloma, A. Journal of Alloys and Compounds 432, 10 (2007).Google Scholar
4 Morikawa, T. Kaneko, K. Higashida, K. Kinoshita, D. Takenaka, M. Kawamura, Y. Materials Transactions 49, 1294 (2008).Google Scholar
5 Kawamura, Y. Yamasaki, M. Materials Transactions 48, 2986 (2007).Google Scholar
6 Yamasaki, M. Anan, T. Yoshimoto, S. Kawamura, Y. Scripta Materialia 53, 799 (2005).Google Scholar
7 Yoshimoto, S. Yamasaki, M. Kawamura, Y. Materials Transactions 47, 959 (2006).Google Scholar
8 Okamura, H. Introduction to Linear Fracture Mechanics, (Baifukan, Tokyo, 1976), p. 218 (in Japanese).Google Scholar
9 Yamaguchi, T. Saito, K. Kawamura, Y.: Journal of Japan Institute of Light Metals 57, 571 (2007).Google Scholar