In-Situ Synthesis of Particle Dispersed Nanocrystalline NiAl By Cryomilling

Published online by Cambridge University Press:  15 February 2011

Benlih Huang ,
J. Vallone ,
C. F. Klein  and
M. J. Luton
Benlih Huang
Affiliation:
Department of Materials Science and Eng., Rutgers University, Piscataway, NJ 08854.
J. Vallone
Affiliation:
Corporate Research, Exxon Research and Engineering Company, Annandale, NJ 08801.
C. F. Klein
Affiliation:
Corporate Research, Exxon Research and Engineering Company, Annandale, NJ 08801.
M. J. Luton
Affiliation:
Corporate Research, Exxon Research and Engineering Company, Annandale, NJ 08801.
Get access

Abstract

The present research was carried out to study the cryogenic synthesis NiAl from elemental powders with the view of forming particle dispersed NiAl. It was found that nanocrystalline NiAl with a crystallite size in the range 5nm to 10nm is produced during cryomilling. Additionally, the nanocrystalline NiAl maintains the fine crystallite size when annealed at high temperatures. It is thought that the resistance of the microstructure to coarsening is due to the presence of nano-scale particles of AIN formed by reaction between milling medium, liquid nitrogen, and aluminum. The transformation of Ni and Al to ordered NiAl was studied using x-ray diffraction. This showed that cryomilling not only produces a solid solution but also can induce in-situ ordering of stoichiometric NiAl. The B2 NiAl structure forms during milling after the elemental powder blend is cryomilled for about 40 hours. It also forms when the “mechanical” solid solution is annealed at room temperature for about twelve hours.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 273: Symposium Q – Intermetallic Matrix Composites II , 1992 , 171
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Luton, M. J., Jayanth, C. S., Disko, M. M., Matras, S., and Vallone, J. in Cryomilling of Nano-crystalline Dispersion Strengthened Aluminum in Multicomponent Ultrafine Microstructures (Mater. Res. Soc. Pro. 132, Pittsburgh PA 1989) pp. 79–86 Google Scholar
2. Massalski, T. B., Binary Alloy Phase Diagrams Vol. 1 (American Society for Metals, Metal Park, Ohio 1987)Google Scholar
3. Whittenberger, J. D., Westfall, L. J., and Nathal, M. V., Scripta Metallurgica 23, 2127 (1989)CrossRefGoogle Scholar
4. Whittenberger, J. D., Arzt, E., and Luton, M. J., J. Mater. Res..5 271 (1990)Google Scholar
5. Gilman, P. S and Benjamin, J. S. in Annual Review on Materials Science Vol. 1, edited by Huggins, R. A., Bube, R. H. and Vermilyea, D. A. (Annual Review Inc., California 1983) p. 279 Google Scholar
6. Huang, B. and Luton, M.J., Unpublished researchGoogle Scholar
7. Ivanov, E., Grigorieva, T., Golubkova, G., Boldyrev, V., Fasman, A.B., Mikhailenko, S. D., and Kalinina, O. T., Materials Letters, 7 (1,2) 51–54 (1988)Google Scholar