In-situ Measurement of GaAs Optical Constants and Surface Quality, as Functions of Temperature

Published online by Cambridge University Press:  16 February 2011

Huade Yao  and
Paul G. Snyder
Huade Yao
Affiliation:
University of Nebraska, Center for Microelectronic and Optical Materials Research, and Department of Electrical Engineering, Lincoln, NE 68588–0511
Paul G. Snyder
Affiliation:
University of Nebraska, Center for Microelectronic and Optical Materials Research, and Department of Electrical Engineering, Lincoln, NE 68588–0511
Get access

Abstract

In-situ spectroscopic ellipsometry (SE) was applied to monitor GaAs (100) surface changes induced at elevated temperatures inside an ultrahigh vacuum (UHV) chamber (<1×10−9 torr base pressure, without As overpressure). The real time data showed clearly the evolution of the native-oxide desorption at ∼577°C, on a molecular-beam-epitaxy (MBE)-grown GaAs (100) surface. In addition, surface degradation was found before and after the oxide desorption. A clean and smooth surface was obtained from an arsenic-capped, MBE-grown GaAs sample, after the arsenic coating was evaporated at ∼350 °C inside the UHV. Pseudodielectric functions <ε>GaAs, from 1.6 eV to 4.5 eV, were obtained through the SE measurements, from this oxide-free surface, at temperatures ranging from room temperature (RT) to ∼610 °C. These <ε> data were used as reference data to develop an algorithm for determining surface temperatures from in-situ SE measurements, thus turning the SE instrument into a sensitive optical thermometer.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 222: Symposium D – Atomic Layer Growth and Processing , 1991 , 87
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Azzam, R.M.A. and Bashara, N.M., Ellipsometry and Polarized Light, (North- Holland, Amsterdam, 1977)Google Scholar
2. Aspnes, D.E., in Handbook of Optical Constants of Solids, edited by Palik, E.D., (Academic Press, New York, 1985) p 89.Google Scholar
3. Aspnes, D.E., Quinn, W.E., and Gregory, S., Appl. Phys. Lett. 56, 2569 (1990).CrossRefGoogle Scholar
4. Yao, H.D., Snyder, P.G. and Woollam, J.A., Proceedings of ICEM-2, 501 (1991).Google Scholar
5. Yao, H.D., Snyder, P.G. and Woollam, J.A., Mat. Res. Soc. Symp. Proc. 202, 339 (in press, 1991).Google Scholar
6. Aspnes, D.E., in Properties of Solids-New Developments, edited by Saraphin, B.O. (North-Holland, Amsterdam, 1976) p799.Google Scholar
7. Aspnes, D.E., J. Vac. Sci. Technol. 17, 1057 (1980).CrossRefGoogle Scholar
8. Yao, H.D., Snyder, P.G., and Woollam, J.A., J. Appl. Phys. (in press, 1991).Google Scholar
9. Lautenschlager, P., Garriga, M., Logothetidis, S., and Cardona, M., Phys. Rev. B 35, 9174 (1987).CrossRefGoogle Scholar
10. Aspens, D.E., Schwartz, G.P., Gualtieri, G.J., Studna, A.A., and Schwartz, B., J. Electrochem. Soc. 128, 590 (1981).CrossRefGoogle Scholar
11. Aspnes, D.E. and Studna, A.A., Phys. Rev. B 27, 985 (1983).Google Scholar
12. Foxon, C.T., Harvey, J.A. and Joyce, B.A., J. Phys. Chem. Solids 34,1693 (1973).Google Scholar
13. The algorithm was programmed by Johs, B., of the J.A. Woollam Co.Google Scholar
14. Johs, B., Meyer, D., Cooney, G., Yao, H.D., Snyder, P.G., Woollam, J.A., Edwards, J. and Maracus, G., Mat. Res. Soc. Symp. Proc. 216, 459 (in press, 1991).Google Scholar
15. Wright, S.L., Marks, R.F. and Goldberg, A.E., J. Vac. Sci. Technol. B 6, 842 (1988).Google Scholar