Highly Reliable Thin Hafnium Oxide Gate Dielectric

Published online by Cambridge University Press:  10 February 2011

Laegu Kang
Affiliation:
Microelectronics Research Center, University of Texas at Austin, Austin, TX 78758, [email protected]
Byoung-Hun Lee
Affiliation:
Microelectronics Research Center, University of Texas at Austin, Austin, TX 78758, [email protected]
Wen-Jie Qi
Affiliation:
Microelectronics Research Center, University of Texas at Austin, Austin, TX 78758, [email protected]
Yong-Joo Jeon
Affiliation:
Microelectronics Research Center, University of Texas at Austin, Austin, TX 78758, [email protected]
Renee Nieh
Affiliation:
Microelectronics Research Center, University of Texas at Austin, Austin, TX 78758, [email protected]
Sundar Gopalan
Affiliation:
Microelectronics Research Center, University of Texas at Austin, Austin, TX 78758, [email protected]
Katsunori Onishi
Affiliation:
Microelectronics Research Center, University of Texas at Austin, Austin, TX 78758, [email protected]
Jack C. Lee
Affiliation:
Microelectronics Research Center, University of Texas at Austin, Austin, TX 78758, [email protected]
Get access

Abstract

HfO2 is the one of the potential high-k dielectrics for replacing SiO2 as a gate dielectric. HfO2 is thermodynamically stable when in direct contact with Si and has a reasonable band gap (∼5.65eV). In this study, MOS capacitors (Pt/HfO2/Si) were fabricated by depositing HfO2 using reactive DC magnetron sputtering in the range of 33∼135Å followed by Pt deposition. During the HfO2 deposition, O2 flow was modulated to control interface quality and to suppress interfacial layer growing. By optimizing the HfO2 deposition process, equivalent oxide thickness (EOT) can be reduced down to ∼11.2 Å with the leakage current as low as 1X10−2 A/cm2 at +1.0V and negligible frequency dispersion. HfO2 films also show excellent breakdown characteristics and negligible hysteresis after high temperature annealing. From the high resolution TEM, there is a thin interfacial layer after annealing, suggesting a composite of Si-Hf-O with a dielectric constant of ≈ 2 X K SiO2.

Type
Research Article
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1]Sze, S.M., Physics of Semiconductor Devices, 2nd ed. (Wiley, New York, 1981).Google Scholar
[2]Hu, C., IEDM Technical digest, 319 (1996).Google Scholar
[3]Wright, P.J., and Saraswat, K.C., IEEE Trans. Electron Dev. 37, 1884 (1990).Google Scholar
[4]Hubbard, K. J. and Schlom, D. G., J. Mater. Res. 15, 2757 (1996).Google Scholar
[5]Nieh, R., Qi, W.J., Jeon, Y. J., Lee, B.H., Lucas, A., Kang, L.G., Lee, J.C., Gardner, M., and Gilmer, M., Material Research Society Spring Meeting (1999).Google Scholar
[6]Luan, H. F., Wu, B. Z., Kang, L. G., Kim, B. Y., Vrtis, R., Roberts, D., and Kwong, D.L., IEDM Technical digest, 609 (1998).Google Scholar
[7]Balog, M., Schieber, M., Michman, M., and Patai, S., Thin Solid Films 41, 247 (1977).Google Scholar
[8]Alers, G.B., Werder, D.J., and Chabal, Y., Appl. Physics Lett. 73, 1517 (1998).Google Scholar
[9]Wilk, G. D. and Wallace, R. M., Appl. Phys. Lett. 74, 2854 (1999).Google Scholar