The Fracture Toughness of a Brittle Nickel Silicide Containing the Ductile Phases Ni(Si) and Ni3Si

Published online by Cambridge University Press:  01 January 1992

Zhaohui Li  and
Erland M. Schulson
Zhaohui Li
Affiliation:
Thayer School of Engineering, Dartmouth College, Hanover, NH 03755
Erland M. Schulson
Affiliation:
Thayer School of Engineering, Dartmouth College, Hanover, NH 03755
Get access

Abstract

The fracture toughness at room temperature of a brittle nickel silicide containing the ductile phases Ni(Si) and Ni3Si has been investigated. The microstructure was comprised of a brittle nickel silicide matrix, ductile Ni(Si) particles distributed within the matrix, and Ni3Si rims around the particles. It was obtained by annealing hot-extruded Ni-23 at.%Si (with and without 0.19 at.% boron) at 1100°C and then air cooling. The fracture toughness values were in the range of 13 MPa m1/2 to 22 MPa m1/2. Systematic effects of annealing time and of boron were not apparent. It would appear that the incorporation of the ductile particles has a beneficial effect on the fracture toughness of an otherwise brittle silicide.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 288: Symposium L – High-Temperature Ordered Intermetallic Alloys V , 1992 , 1081
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Ashby, M. F., Blunt, F. J., and Bannister, M., Acta Metall., 1989, Vol. 7, pp 1847–57.Google Scholar
2. Mendiratta, M.G., Lewandowski, J.J., and Dimiduk, D.M., Metall. Trans A, 1991, Vol. 22A, July, pp 1573–83.Google Scholar
3. Sigl, L.S., Mataga, P.A., Dalgleish, B.J., McMeeking, R.M., and Evans, A.G., Acta Metall., 1988, Vol. 36 (4), pp. 945–53.Google Scholar
4. Sigl, L.S. and Exner, H.E., Metall. Trans. A, 1987, Vol. 18A, pp. 1299–1308.Google Scholar
5. Krstic, V.D., Phil. Mag., 1983, Vol. 48 (5), pp. 695–708.Google Scholar
6. Elliott, C.K., Odette, G.R., Lucas, G.E., and Sheckherd, J.W.: High Temperature, High Performance Composites, MRS Proc., Lemkey, , ed., Materials Research Society, Pittsburgh, PA, 1988, Vol. 120, pp. 95–101.Google Scholar
7. Schulson, E. M., Briggs, L. J. and Baker, I., Acta. Metall. Mater, vol. 38, No. 2, pp 207–213, 1990.Google Scholar
8. Nose, T. and Fujii, T., J. Am. Ceram. Soc., Vol. 71, No. 5, 328–33 (1988).Google Scholar
9. Quantitative Microscopy, DeHoff, R. T. and Rhines, F. N., eds., McGraw - Hill, Inc., New York, NY, 1968.Google Scholar
10. Binary Alloy Phase Diagrams, Ed-T.B. Massalski, ASM, (1986) pl754.Google Scholar
11. Baker, I., Yuan, J. and Schulson, E. M., Metall Transactions A (in press).Google Scholar
12. Li, Zhaohui, M.S. Thesis, Thayer School of Engineering, Dartmouth College. (1992).Google Scholar
13. Ravichandran, K.S., Scripta Metall., Vol. 26, pp. 1389–1393 (1992).Google Scholar
14. Tabor, D.: Hardness of Metals, Clarenden Press, London, 1951.Google Scholar