Formation Process of a Rhenium-Based Diffusion Barrier on a Nickel-Based Superalloy

Published online by Cambridge University Press:  26 February 2011

Yongming Wang ,
Somei Ohnuki  and
Toshio Narita
Yongming Wang
Affiliation:
[email protected], Hokkaido University, Materials Science Division, N-13, W-8, Kita-Ku, Sapporo, 060-8628, Japan
Somei Ohnuki
Affiliation:
[email protected], Graduate School of Engineering, Materials Science Division, N-13, W-8, Kita-Ku, Sapporo, 060-8628, Japan
Toshio Narita
Affiliation:
[email protected], Graduate School of Engineering, Materials Science Division, N-13, W-8, Kita-Ku, Sapporo, 060-8628, Japan
Get access

Abstract

The formation process of Rhenium-based diffusion barrier coating on Nickel-based superalloy has been investigated in present paper. The diffusion barrier can be formed by two steps, electroplating and Cr cementation. A tri-layer film structure consisting of Ni / Re~63Ni~37 / Ni was prepared by electrolytic plating onto the substrate of a Ni-based single-crystal superalloy, it was found that the Re-Ni plating film composed of amorphous alloy which is characterized by X-ray diffraction (XRD) analysis. The changes of the barrier films which formed by followed Cr-Pack cementations at 1573 K for 20 min, 50 min, 240 min, 360 min and 600 min, respectively, were investigated by Scan Electron Microscope (SEM) and Electron Probe Micro Analyzer (EPMA). Changing in the thickness of barrier film exhibited two stages, and the composition of barrier film changed along the curve of solubility limit of Ni in Re-Ni-Cr sigma phase.

Keywords

diffusionRecoating
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 980: Symposium II – Advanced Intermetallic-Based Alloys , 2006 , 0980-II05-29
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Narita, T.: High Temp. Soc. 28(2002) 135–143.Google Scholar
2. Pomeroy, M. J.: Mater. and Design 26(2005) 223–231.Google Scholar
3. Hino, T., Ishiwata, Y., Yoshioka, Y., Nagata, K., Kobayashi, T., Koizumi, Y., Harada, H. and Yamagata, T.: Proc. Int. Cong. on Gas Turbine, (Kobe, 1999) pp. 169–174.Google Scholar
4. Narita, T., Hayashi, S., Lang, F. and Thosin, K. Z.: Mater. Sci. Forum 502(2005) 99–104.Google Scholar
5. Slyusarenko, E. M., Peristyi, A. V., Kerimov, E.Yu., Sofin, M. V. and Skorbov, D. Yu.: Alloys and Comp. 264(1998) 180–189.Google Scholar
6. Rae, C. M. F. and Reed, R. C.: Acta Mater. 49(2001) 4113–4125.10.1016/S1359-6454(01)00265-8Google Scholar