Fabrication of Conductive Glass Nanocomposites with Networks of Antimony Tin Oxide

Published online by Cambridge University Press:  05 June 2013

Timothy L. Pruyn
Affiliation:
School of Materials Science and Engineering, Georgia Institute of Technology Atlanta, GA 30332-0245, U.S.A.
Rosario A. Gerhardt
Affiliation:
School of Materials Science and Engineering, Georgia Institute of Technology Atlanta, GA 30332-0245, U.S.A.
Get access

Abstract

The percolation threshold in a ceramic composite depends on the processing conditions used to fabricate them along with the size and shape of the filler. In this study, borosilicate glass microspheres were used as the matrix material and nanosized antimony tin oxide (ATO) particles were used as the filler. The microsphere/ATO composites were fabricated by hot pressing around the glass transition temperature in order to control the viscosity. The pressure and temperature applied allowed the ATO to be confined to the spaces between certain glass particles, forming percolating networks at low volume fractions of the ATO. The electrical properties were examined using ac impedance spectroscopy. The impedance, electric modulus, and tan δ were studied which allowed for valuable insights in structure-property-processing relationships in these materials, along with determination of the percolation behavior in these composites. This analysis on samples right before percolation indicated that there was a highly resistive component affecting long range conductivity which is likely due to porosity at the triple points while the dielectric response is affected by the clusters of ATO nanoparticles. Based on this, the percolation of ATO should reduce down to lower concentrations if the processing conditions are improved to reduce this porosity and further segregate the ATO.

Type
Articles
Copyright
Copyright © Materials Research Society 2013 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Nan, C.-W., Shen, Y. and Ma, J., Annual Review of Materials Research 40(1), 131151 (2010).CrossRefGoogle Scholar
Gerhardt, R.A., Runyan, J., Sana, C.R., Ruh, R., J. Am. Ceram.Soc. 84(10), 23352342(2001).CrossRefGoogle Scholar
Ou, R. Q., Gupta, S., Parker, C. A. and Gerhardt, R. A., J. Phys. Chem. B 110(45), 2236522373 (2006).CrossRefGoogle Scholar
Capozzi, C. J., Li, Z., Samuels, R. J. and Gerhardt, R. A., J. Appl. Phys. 104(11), 14902–1-14902-10 (2008).CrossRefGoogle Scholar
Capozzi, C. J. and Gerhardt, R. A., Adv. Funct. Mater. 17(14), 25152521 (2007).CrossRefGoogle Scholar
Varshneya, A. K., Fundamentals of Inorganic Glasses. (The Society of Glass Technology, Sheffield, 2006).Google Scholar
Zhang, J. R., Gao, L. and Chen, M. H., J. Am. Ceram. Soc. 89(12), 38743876 (2006).CrossRefGoogle Scholar
Andres-Verges, M. and West, A. R., Journal of Electroceramics 1(2), 125132 (1997).Google Scholar
Gerhardt, R., Journal of Physics and Chemistry of Solids 55(12), 14911506 (1994).CrossRefGoogle Scholar
Cao, W. and Gerhardt, R., Solid State Ionics 42(3–4), 213221 (1990).CrossRefGoogle Scholar
Waddell, J., Ou, R., Capozzi, C. J., Gupta, S., Parker, C. A., Gerhardt, R. A., Seal, K., Kalinin, S. V. and Baddorf, A. P., Appl. Phys. Lett. 95(23), 233122–1-233122-3 (2009).CrossRefGoogle Scholar