Fabrication of Carbon Nanotube Field-Effect Transistors with Metal and Semiconductor Electrodes

Published online by Cambridge University Press:  01 February 2011

Himani Sharma
Affiliation:
Alabama A & M University, Electrical Engineering, 4900 Meridian Street, Normal, AL, 35762, United States, 256-372-5679
Zhigang Xiao
Affiliation:
[email protected], Alabama A & M University, Department of Electrical Engineering, 4900 Meridian Street, Normal, AL, 35762, United States
Get access

Abstract

Carbon nanotube field-effect transistors (CNTFETs) were fabricated with metal material (gold) and semiconductor material (bismuth telluride) as the source and drain materials. Highly-purified HiPCO-grown single-walled carbon nanotubes (CNTs) from Carbon Nanotechnologies, Inc. (CNI) were used for the fabrication of CNTFETs. The single-walled carbon nanotubes were ultrasonically dispersed in toluene and dimethylformamide (DMF) with trifluoroacetic acid (TFA), as co-solvent. Dielectrophoresis (DEP) method was used to deposit, align, and assemble carbon nanotubes (CNTs) to bridge the gap between the source and drain of CNTFETs to form the channel. The structure of CNTFET is similar to a conventional field-effect transistor with substrate acting as a back-side gate. Electron-beam evaporation was used to deposit gold and bismuth telluride thin films. Microfabrication techniques such as photolithography, e-beam lithography, and lift-off process were used to define and fabricate the source, drain, and gate of CNTFETs. The gap between the source and drain varied from 800 nm to 3 µm. The drain-source current (IDS) of the fabricated CNTFETs versus the drain-source voltage (VDS) and the gate voltage (VG) was characterized. It was found that in the case of gold (Au) electrodes, the IV curves of CNTFETs clearly show behavior of the CNT (metallic or semiconducting) aligned across the source and drain of CNTFETs, while in the case of bismuth telluride (Bi2Te3) electrodes, the I-V curves are less dependent on the type of CNTs (metallic or semiconducting). The developed carbon nanotube field-effect transistors (CNTFETs) can be a good candidate for the application of nanoelectronics and integrated circuits with a high mobility and fast switching.

Type
Research Article
Copyright
Copyright © Materials Research Society 2008

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Wong, E. W., Sheehan, P. E. and Lieber, C. M., Science 277, 1971 (1997).Google Scholar
2. Tans, S. J., Devoret, M. H., Dai, H. J., Thess, A., Smalley, R. E., Geerligs, L.J. and Dekker, C., Nature 386, 474 (1997).Google Scholar
3. Rueckes, T., Kim, K., Joselevich, E., Tseng, G.Y., Cheung, C. and Lieber, C.M., Science 289, 94 (2000).Google Scholar
4. Biercuk, M.J., Mason, M. and Marcus, C.M., Nano Lett. 4, 1 (2004).Google Scholar
5. Bachtold, A., Hadley, P., Nakanishi, T. and Dekker, C., Science 294, 1317 (2001).Google Scholar
6. Kong, J., Franklin, N.R., Zhou, C., Chapline, M.G., Peng, S., Cho, K. and Dai, H., Science 287, 622 (2000).Google Scholar
7. Besteman, K., Lee, J., Wiertz, F.G.M., Heering, H.A. and Dekker, C., Nano Lett. 3,727 (2003).Google Scholar
8. Yao, Z., Kane, C.L. and Dekker, C., Phys. Rev. Lett. 84, 2941 (2000).Google Scholar
9. Tans, S.J., Verschueren, A., Dekker, C.: Tans, S.J., Verschueren, A. and Dekker, C., Nature 393, 49 (1998).Google Scholar
10. Bockrath, M., Cobden, D.H., Lu, J., Rinzler, A.G., Smalley, R.E., Balents, L. and McEuen, P.L. Nature 397, 598 (1999).Google Scholar
11. Kong, J., Soh, H., Cassell, A., Quate, C. and Dai, H., Appl. Phys. A 69, 305 (1999).Google Scholar
12. Liu, , Casavant, M.J., Cox, M., Walters, D.A., Boul, P., Lu, W., Rimberg, A.J., Smith, K.A., Colbert, D.T. and Smalley, R.E., Chem. Phys. Lett. 303, 125 (1999)Google Scholar
13. Krupke, R., Malik, S., Weber, H.B., Hampe, O., Kappes, M.M. and Löhneysen, H. V., Nano. Lett. 2, 1161 (2002).Google Scholar
14. Chen, X.Q., Saito, T., Yamada, H. and Matsushige, K., Appl. Phys. Lett. 78, 3714 (2001).Google Scholar
15. Yamamoto, K., Akita, S. and Nakayama, Y.J., Phys. D: Appl. Phys. 31, L34 (1998).Google Scholar
16. Krupke, R., Hennrich, F., Weber, H. B., Beckmann, D., Hampe, O., Malik, S., Kappes, M.M. and Löhneysen, H.V., Appl. Phys. A 76, 397 (2003).Google Scholar
17. Chen, H., Muthuraman, H., Stokes, P., Zou, J., Liu, X., Wang, J., QunHuo, , Khondaker, S.I. and Zhai, L., Nanotechnology 18, 415606 (2007).Google Scholar
18. Li, J., Zhang, Q., Yang, D. and Tian, J., Carbon 42, 2263 (2004)Google Scholar
19. Collins, P.G., Arnold, M. S. and Avouris, Ph., Science 292, 706 (2001).Google Scholar
20. Collins, P.G., Hersam, M., Arnold, M., Martel, R., Avouris, Ph., Phys Rev Lett, 86,3128 (2001).Google Scholar