Fabrication and Properties of Si3N4 with Rare Earth Apatite Grain Boundary Phases

Published online by Cambridge University Press:  25 February 2011

Terry N. Tiegs ,
Stephen D. Nunn ,
Kristin L. Ploetz ,
Paul A. Menchoffer  and
Claudia A. Walls
Terry N. Tiegs
Affiliation:
Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, Tennessee 37831-6087
Stephen D. Nunn
Affiliation:
Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, Tennessee 37831-6087
Kristin L. Ploetz
Affiliation:
Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, Tennessee 37831-6087
Paul A. Menchoffer
Affiliation:
Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, Tennessee 37831-6087
Claudia A. Walls
Affiliation:
Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, Tennessee 37831-6087
Get access

Abstract

The rare earth-oxide and nitride apatites were examined as grain boundary phases in silicon nitride to assess their potential for developing high toughness materials using gas-pressuresintering. Densification was dependent on the quantity of additives used with high densities achieved at equivalent oxygen contents of ∼8%. Fracture toughnesses (KIc) up to 8-10 MPa√m were obtained for some compositions. Ambient temperature flexural strengths were in the range of 400-720 MPa; however, the strengths atelevated temperatures (1200ºC) were reduced from these values.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 287: Symposium K – Silicon Nitride Ceramics–Scientific and Technological Advances , 1992 , 353
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Lange, F. F., “Relation Between Strength, Fracture Energy and Microstructure of Hot-Pressed Si3N4 ,” J. Am. Ceram. Soc., 56 [10] 518–522 (1973)Google Scholar
2. Tani, E., Umebayashi, S., Kishi, K., Kobayashi, K., and Nishijima, M., “Gas-Pressure Sintering of Si3N4 With Concurrent Addition of Al2O3 and 5 wt % Rare Earth Oxide: High Fracture Toughness with Fiber-Like Structure,” Am. Ceram. Soc. Bull., 65[9] 1311–1315(1986)Google Scholar
3. Li, C. and Yamanis, J., “Super-Tough Silicon Nitride With R-Curve Behavior,” Ceram. Eng. Sci. Proc., 10[7-8]632–645(1989)Google Scholar
4. Matsuhiro, K. and Takahashi, T., “The Effect of Grain Size on the Toughness of Sintered Si3N4 ,” Ceram. Eng. Sci. Proc., 10[7-8]807–816(1989)Google Scholar
5. Kawashima, T., Okamoto, H., Yamamoto, H., and Kitamura, A., “Grain Size Dependence of the Fracture Toughness of Silicon Nitride Ceramics,” J. Ceram. Soc. Japan (1991)Google Scholar
6. Mitomo, M., “Pressure Sintering of Si3N4 ,” J. Mater. Sci., 11, 1103–1107 (1976)Google Scholar
7. Priest, H. F., Priest, G. L., and Gazza, G. E., “Sintering of Si3N4 Under High Nitrogen Pressure,” J. Am. Ceram. Soc., 60 [1-2] 81–85 (1977)Google Scholar
8. Drew, P. and Lewis, M. H., “The Microstructures of Silicon Nitride Ceramics During Hot- Pressing Transformations,” J. Mater. Sci., 9, 261–269 (1974)Google Scholar
9. Lewis, M. H., Leng-Ward, G., and Jasper, C., “Sintering Additive Chemistry in Controlling Properties of Nitride Ceramics,” pp. 1019–1033 in Ceramic Transactions, Ceramic Powder Science, H, B., Edited by Messing, G. L., Fuller, E.R. Jr, and Hausner, H.. American Ceramic Society, Westerville, OH (1988)Google Scholar
10. Thompson, D. P., “Alternative Grain-Boundary Phases for Heat-Treated Si3N4 and B'-Sialon Ceramics,” Brit. Ceram. Proc.,45, 1–13 (1990)Google Scholar
11. Wittmer, D. E., “Alternative Processing Through Turbomilling,” Am. Ceram. Soc. Bull., 67[10]1670–1672 (1988)Google Scholar
12. Hattori, Y., Tajima, Y., Yabuta, K., Matsuo, J., and Watanabe, T., “Gas Pressure Sintered Silicon Nitride Ceramics for Turbocharger Applications,” pp. 165–172 in Proc. 2nd Internat. Symp. on Ceramic Materials and Components for Engines, Edited by Bunk, W. and Hausner, H., Verlag Deutsche Keramische Gesellschaft, Bad Honnef, FRG (1986).Google Scholar
13. Anstis, G. R. et al. , “A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: I, Direct Crack Measurements,” J. Am. Ceram. Soc., 64[9]533–538(1981).Google Scholar
14. Chantikul, P. et al. , “A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: II, Strength Method,” J. Am. Ceram. Soc., 64[9]539–543(1981).Google Scholar
15. 24. Lange, F. F., Singhal, S. C., and Kuznicki, R. C., “Phase Relationships and Stability Studies in the Si3N4 -SiO2-Y2O3 Pseudoternary,” J. Amer. Ceram. Soc., 60 (5-6), 249–252 (1977)Google Scholar