Electromigration In Submicron Wide Copper Lines

Published online by Cambridge University Press:  15 February 2011

O. V. Kononenko ,
V. N. Matveev ,
Yu. I. Koval ,
S. V. Dubonos  and
V. T. Volkov
O. V. Kononenko
Affiliation:
Institute of Microelectronics Technology & High Purity Materials, Russian Academy of Sciences, Chernogolovka 142432, Moscow District, Russia
V. N. Matveev
Affiliation:
Institute of Microelectronics Technology & High Purity Materials, Russian Academy of Sciences, Chernogolovka 142432, Moscow District, Russia
Yu. I. Koval
Affiliation:
Institute of Microelectronics Technology & High Purity Materials, Russian Academy of Sciences, Chernogolovka 142432, Moscow District, Russia
S. V. Dubonos
Affiliation:
Institute of Microelectronics Technology & High Purity Materials, Russian Academy of Sciences, Chernogolovka 142432, Moscow District, Russia
V. T. Volkov
Affiliation:
Institute of Microelectronics Technology & High Purity Materials, Russian Academy of Sciences, Chernogolovka 142432, Moscow District, Russia
Get access

Abstract

Copper films were deposited onto oxidized silicon wafers by the self-ion assisted technique. A 0 and 6 kV bias was applied to the substrate during the deposition. The films were patterned into parallel line arrays of 20 lines 0.5 mm long, using electron lithography and dry etching. After patterning, the lines were covered by silicon oxide and annealed in vacuum for 1 hour at the temperature 450° C. Electromigration testing was performed in air in the temperature range from 280° to 350° C and at a current density 3.106 A/cm2.

It was found that the resistivities of the films deposited at 6 kV and without bias were 1.7 and 2.0 μΩ-cm, respectively. The median times to failure are 398.6 and 240 h and the deviations in the time to failure are 0.8 and 0.54 for 6 kV lines and 0 kV lines, respectively. An electromigration activation energy of 0.89 eV was found for 0 kV films.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 428: Symposium L – Materials Reliability in Microelectronics VI , 1996 , 61
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Tao, J., Cheung, N.W., and Hu, C., IEEE Electron Device Letters 14, 249 (1993).Google Scholar
2. Fionova, L.K., Kononenko, O.V., and Matveev, V.N., Scripta Metallurgica et Materialia 27, 329(1992).Google Scholar
3. Fionova, L.K., Kononenko, O.V., and Matveev, V.N., Thin Solid Films 227 (1993) 54.Google Scholar
4. Bai, P., Yang, G.-R., Lu, T.-M., and Lau, L.W.M., J. Vac. Sci. Technol. A, 8, 1465 (1990).Google Scholar
5. Kononenko, O.V., and Matveev, V.N., Mat. Res. Soc. Symp. Proc. 356, Thin films: Stresses and Mechanical Properties V. Ed. by Baker, S.P., Borgesen, P., Townsend, P.H., Ross, C.A., Volkert, C.A..Google Scholar
6. Kononenko, O.V., Ivanov, E.D., Matveev, V.N., and Khodos, I.I., Scripta Metallurgica et Materialia 33, 1981 (1995).Google Scholar
7. Kononenko, O.V., Matveev, V.N., Kasumov, A.Yu., Kislov, N.A., and Khodos, I.I., Vacuum 46, 685 (1995).Google Scholar
8. Barna, A., Barna, P.B., Radnoczi, G., Reicha, F.M., and Toth, L., Phys. stat. sol. (a), 55, 427 (1979).Google Scholar