Effect of Thermal Residual Stress on the Mechanical Properties of NiAl-Based Composites

Published online by Cambridge University Press:  10 February 2011

Hahn Choo ,
Mark Bourke  and
Philip Nash
Hahn Choo
Affiliation:
Manuel Lujan Jr. Neutron Scattering Center, Los Alamos National Laboratory, Los Alamos, NM, 87545, USA, [email protected]
Mark Bourke
Affiliation:
Manuel Lujan Jr. Neutron Scattering Center, Los Alamos National Laboratory, Los Alamos, NM, 87545, USA, [email protected]
Philip Nash
Affiliation:
Dept. of Mechanical, Materials and Aerospace Engineering, Illinois Institute of Technology, Chicago, IL, 60616, USA
Get access

Abstract

NiAl-based hybrid composites containing 5, 15 and 30 volume percent of A12O3 fibers in addition to AIN dispersion particles were fabricated via a powder metallurgy route. The strengthening mechanisms associated with the short A12O3 fiber in NiAl-(A1N)dispersion,-(A12O3)fiber, composite were studied with an emphasis on the effect of thermal residual stress on the compressive strength at room temperature and 1300K. At 300K, the yield strength of the composites was predicted using a linear superposition of the monolithic yield strength, direct fiber strengthening and tensile matrix residual stresses. The prediction shows good agreement with the measured data. The majority of the room temperature strengthening is attributable to the residual stress. At 1300K, the strengthening was achieved only by the load sharing of the fibers and there is no direct influence from the process-induced thermal residual stresses since they were completely relaxed at this temperature.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 552: Symposium KK – High-Temperature Ordered Intermetallic Alloys VIII , 1998 , KK5.22.1
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Whittenberger, J.D., Artz, E. and Luton, M.J., J. Mater. Res. 5, 2819 (1990).Google Scholar
2. Wu, S., PhD thesis, Illinois Institute of Technology, 1996.Google Scholar
3. Choo, H., Nash, P. and Dollar, M., in Processing and Fabrication of Advanced Material V, edited by Srivatsan, T.S. and Moore, J.J. (TMS, Warrendale, PA, 1996) pp. 361–377 Google Scholar
4. Choo, H., Nash, P., and Dollar, M., Mater. Sci. Eng. A239–240, 464 (1997).Google Scholar
5. Nathal, M.V. and Ebert, L.J., Metall. Trans. A 16A, 427 (1985).CrossRefGoogle Scholar
6. Zhu, Y.T. and Blumenthal, W.R., in Micromechanics of Advanced materials, edited by Chu, S.N.G. (TMS, Warrendale, PA, 1995) pp. 481–485.Google Scholar
7. Arsenault, R.J. and Taya, M., Acta Metall. 35, 651 (1987).CrossRefGoogle Scholar
8. Arsenault, R.J., Wang, L. and Feng, C.R., Acta Metall. 39, 47 (1991).CrossRefGoogle Scholar
9. Bourke, M.A.M., Goldstone, J.A. and Holden, T.M., in Measurement of Residual and Applied Stress Using Neutron Diffraction, edited by Hutchings, M.T. and Krawitz, A.D. (Kluwer Academic Publishers, Netherlands, 1992) pp. 369–382.CrossRefGoogle Scholar
10. Majumdar, S., Singh, J.P., Kupperman, D. and Krawitz, A.D., J. Eng. Mater. Tech. 113, 51 (1991).CrossRefGoogle Scholar
11. Choo, H., Bourke, M., Daymond, M. and Nash, P. (in preparation).Google Scholar
12. Choo, H., PhD thesis, Illinois Institute of Technology, 1998.Google Scholar
13. Wilson, D.M., Lieder, S.L. and Lueneburg, D.C., in Intermetallic Matrix Composites III, edited by J.A. Graves (Mater.Res.Soc.Proc. 350, Pittsburgh, PA, 1994) pp. 89–98.Google Scholar
14. Kelly, A. and Street, K.N., Proc. R. Soc. Lond. A. 328, 283 (1972).Google Scholar
15. Whittenberger, J.D., Kumar, K.S. and Mannan, S.K., Mater. at High Temp. 9, 3 (1991).Google Scholar