Effect of CdCl2 Treatment Conditions on the Deep Level Density, Carrier Lifetime and Conversion Efficiency of CdTe Thin Film Solar Cells

Published online by Cambridge University Press:  21 March 2011

A. Sandhu ,
K. Kobayashi ,
T. Okamoto ,
A. Yamada  and
M. Konagai
A. Sandhu
Affiliation:
Tokai University, Dept of Electrical Engineering, 1117 Kita-kaname, Hiratsuka-shi, Kanagawa 239-1292, Japan
K. Kobayashi
Affiliation:
Tokai University, Dept of Electrical Engineering, 1117 Kita-kaname, Hiratsuka-shi, Kanagawa 239-1292, Japan
T. Okamoto
Affiliation:
Dept of Physical Electronics, Tokyo Institute of Technology, 2-12-1 O-okayama, Meguro-ku, Tokyo 152-8552, Japan
A. Yamada
Affiliation:
Dept of Physical Electronics, Tokyo Institute of Technology, 2-12-1 O-okayama, Meguro-ku, Tokyo 152-8552, Japan
M. Konagai
Affiliation:
Dept of Physical Electronics, Tokyo Institute of Technology, 2-12-1 O-okayama, Meguro-ku, Tokyo 152-8552, Japan
Get access

Abstract

The effect of CdCl2 annealing conditions of glass/TCO/n/CdS/p-CdTe solar cell structures on the deep level density and carrier lifetime of the p-CdTe layer and correlation with the solar cell conversion efficiency was investigated. CdCl2 treatment was carried out at temperatures ranging from 370 to 460°C for 15 min. A clear correlation between trap density, carrier lifetime, conversion efficiency and the CdCl2 annealing conditions was observed. Un-annealed structures had a conversion efficiency of 5.7%, hole trap energy of EV+0.42eV, hole trap density of 8.71×1014cm−3, and decay lifetime of 0.15μs. The optimum CdCl2 annealing temperature was found to be 415°C for structures grown at a substrate temperature of 595°C, where the conversion efficiency, hole trap energy, hole trap density, decay lifetime were 13.4%, EV+0.44eV, 8.10×1012 cm−3 and 0.40μs, respectively.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 668: Symposium H – II-IV Compound Semiconductor Photovoltaic Materials , 2001 , H8.13
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Okamoto, T., Harada, Y., Yamada, A., Konagai, M., Sol. Energy Mat. & Sol. Cells, 67, 187 (2001)Google Scholar
[2] Ringel, S. A., Smith, A. W., MacDougel, M. H., Rohatgi, A., J. Appl. Phys. 70, 881 (1991)Google Scholar
[3] McCandless, B. E., Moulton, L. V. and Birkmire, R. W., Prog. Photovolt. Res. Appl. 5, 247 (1997)Google Scholar
[4] Vos, De, Parrot, J. E., Baruch, P., Landsberg, P. T., Proceddings of the 14th European Photovoltaic Solar Cell Energy Conf., Amsterdam, 1315 (1994)Google Scholar
[5] Okamoto, T., Yamada, A., and Konagai, M., J. Cryst. Growth, 214/215, 1148 (2000)Google Scholar
[6] Horanyi, T., Pavelka, T., Tutto, P., Applied Surface Science, 63, 306 (1993)Google Scholar
[7] Lourenco, M.A., Yew, Y.K., Homewood, K.P., Durose, K., Richter, H., and Bonnet, D., J. Appl. Phys. 82, 1423 (1997)Google Scholar