Devitrification Behavior of SRL Defense Waste Glass

Published online by Cambridge University Press:  25 February 2011

Dennis F. Bickford  and
Carol M. Jantzen
Dennis F. Bickford
Affiliation:
E. I. du Pont de Nemours & Co., Savannah River Laboratory Aiken, South Carolina 29808
Carol M. Jantzen
Affiliation:
E. I. du Pont de Nemours & Co., Savannah River Laboratory Aiken, South Carolina 29808
Get access

Abstract

Simulated SRL waste was prepared with compositions varying in iron and aluminum content. Two batches with similar composition were produced with different amounts of reducing agent added. Samples were isothermally heat treated and used to derive time-temperature-transformation diagrams. Supplementary samples were cooled in a manner programmed to simulate the cooling curves of production canisters. Less than 10% total devitrification occurs during normal processing. However, when waste glass 165 was purposely devitrified, un to 30 volume percent total spinel and acmite formed. Formation of these species had minor effect on leachability in MCC-1 and accelerated leach tests.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 26: Symposium D – Scientific Basis for Nuclear Waste Management VII , 1983 , 557
Copyright
Copyright © Materials Research Society 1984

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Raines, G.E., Rickertsen, L.D., Claiborne, H.C., McElroy, J.L., and Lynch, R.W., Scientific Basis for Nuclear Waste Management, 3, Plenum Press, NY (1981).Google Scholar
2. Turcotte, R.P., and Wald, J.W., PNL-2247, Pacific Northwest Laboratory, Richland, WA (1978).Google Scholar
3. Turcotte, R.P., Wald, J.W., and May, R.P., Scientific Basis for Nuclear Waste Management, 2, Plenum Press, NY, 141-148 (1980).Google Scholar
4. Onorato, P.I.K. and Uhlmann, D.R., J. Non-Crystalline Solids, 22, 367–378 (1976).Google Scholar
5. Jantzen, C.M., Bickford, D.F., and Karraker, D.G., Proceedings of Second International Symposium on Ceramics in Nuclear Waste Management, American Ceramics Society (1983).Google Scholar
6. Schreiber, H D.,etal “An Electromotive Force Series in a Borosilicate Glass-Forming Melt,” submitted for publication in Science, January 1984.Google Scholar
7. Jantzen, C.M. and Karraker, D.G., “Quantative X-ray Diffraction and Magnetic Susceptibility for Devitrification Studies,” to be published in Journal of American Ceramic Society.Google Scholar
8. Strachan, D.M., Barnes, B.O., and Turcotte, R.P., Scientific Basis for Nuclear Waste Management, 3 Plenum Press, NY, 347–354 (1981).Google Scholar
9. Shewmon, P.G., Transformations in Metals, McGraw Hill, Inc., New York (1969)Google Scholar
10. Minaev, A.A., Oziraner, S.N., and Prokhorova, N.P., Ceramics in Nuclear Waste Management, Conf-790420, 229-232 (1979).Google Scholar
11. Beall, G.W. and Rittler, H.L., Am. Ceram. Soc. Bull, 55, [6], 579–582 (1976).Google Scholar
12. Jackson, K.A., Liquid Metals and Solidification, 174, ASM, Cleveland (1958).Google Scholar
13. Guber, W., Hussain, M., Kahl, L., Muller, W., Saidl, J., Ceramics in Nuclear Waste Management, Conf-790420, 285 192 (1979).Google Scholar
14. Dalton, J.T., Boult, K.A., Chamberlain, H.E., and Marples, J.A.C., Proceedings of Intl. Seminar on Chemistry and Process Engineering for High Level Liquid Waste Solidification, Julich, W. Germany, July-Conf 42, 515–532 (1982).Google Scholar
15. Malow, A., Ceramics in Nuclear Waste Management, Conf-790420, 203–209 (1979).Google Scholar
16. Hench, L.L. and Clark, D.E., NUREG/CR-3472, 347–354 Vol. 1 (1983).Google Scholar
17. Bibler, N.E., Glastechn. Ber, 56K, 736–742 (1983).Google Scholar