Crystallization Kinetics Of Metallo-Organics Derived Pzt Thin Film

Published online by Cambridge University Press:  28 February 2011

K.C. Chen  and
J. D. Mackenzie
K.C. Chen
Affiliation:
University of California, Los Angeles, Dept. of Materials Science and Engineering, Los Angeles, CA 90024 Current address: General Atomics, PO Box 85608, San Diego, CA 92138–5608
J. D. Mackenzie
Affiliation:
University of California, Los Angeles, Dept. of Materials Science and Engineering, Los Angeles, CA 90024
Get access

Abstract

PZT films on fused silica substrates were prepared by a multiple dipping-firing process from a stable solution of titanium isopropoxide, zirconium n-propoxide and lead 2- ethylhexanoate. The crystallization kinetics of the amorphous PZT films was studied by quantitative X-ray analysis. The crystallization of the amorphous film to perovskite phase involved a transitional pyrochlore structure phase. The entire crystallization was described by a consecutive phase transformation process in which nucleation dominated.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 180: Symposium A – Better Ceramics Through Chemistry IV , 1990 , 663
Copyright
Copyright © Materials Research Society 1990

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Yoshikawa, Y. and Tsuzuki, K., J. Amer. Ceram. Soc. 73, 31 (1990).Google Scholar
2. Yamaguchi, O. et al. , J. Amer. Ceram. Soc. 72, 1065 (1989);Google Scholar
2a. J. Amer. Ceram. Soc. 69, C-256 (1986);Google Scholar
2b. J. Amer. Ceram. Soc. 69. C-20 (1986);Google Scholar
2c. J. Amer. Ceram. Soc. 67. C-150 (1986);Google Scholar
2d. J. Amer. Ceram. Soc. 68. C-173 (1985).Google Scholar
3. Shaikh, A. S. and Vest, G. M., J. Amer. Ceram. Soc. 69, 682 (1986).Google Scholar
4. Grucovich, S. R. and Blum, J. B., Ferroelectric 62, 189 (1985).Google Scholar
5. Fukushima, J., Kodaira, K. and Matsushita, T., J. Mater. Sci. 19, 595 (1984).Google Scholar
6. Lipelles, R. A. and Coleman, D. J. in Ultrastructure Processing of Advanced Ceramics, Eds. by Mackenzie, J. D. and Ulrich, D. R., John Wiley and Sons, N. Y. (1988) 919.Google Scholar
7. Schroeder, H., in Physics of Thin Films Vol. 5, Hass, G. and Hass, R. E. Eds. Academic Press, N. Y. (1969) pp. 87–141.Google Scholar
8. Chaklader, A.C.D. and Roberts, A. L., J. Amer. Ceram. Soc. 44, 35 (1961).Google Scholar