The control of gold nanocluster sizes in dielectric thin films via ion beam assisted deposition

Published online by Cambridge University Press:  17 March 2011

S. Schiestel
Affiliation:
George Washington University, Washington, DC 20052 Naval Research Laboratory, Code 6370, Washington, DC 20375, USA
C.A. Carosella
Affiliation:
George Washington University, Washington, DC 20052 Naval Research Laboratory, Code 6370, Washington, DC 20375, USA
G.K. Hubler
Affiliation:
George Washington University, Washington, DC 20052 Naval Research Laboratory, Code 6370, Washington, DC 20375, USA
S.B. Qadri
Affiliation:
George Washington University, Washington, DC 20052 Naval Research Laboratory, Code 6370, Washington, DC 20375, USA
D. Knies
Affiliation:
George Washington University, Washington, DC 20052 Naval Research Laboratory, Code 6370, Washington, DC 20375, USA
R.M. Stroud
Affiliation:
George Washington University, Washington, DC 20052 Naval Research Laboratory, Code 6370, Washington, DC 20375, USA
Get access

Abstract

Gold nanoclusters in silica were deposited by co-evaporation of gold and silica in the presence of an argon ion beam. Gold clusters are formed in-situ during the deposition process. The damage induced by the ion beam controls the cluster size, and clusters with a diameter between 15 – 30 Å are obtained. The Au clusters show a highly compressive strain as measured by X-ray diffraction and lattice parameters up to 3.5 % smaller than in bulk gold are observed. Post- deposition annealing in air leads to cluster growth and release of the strain. Annealing near the melting point of gold causes the clusters to grow exponentially up to 180 Å. This is accompanied by a blue shift of the Mie absorption peak. Furthermore the formation of a superlattice was observed by TEM and confirmed by small angle XRD measurements.

Type
Research Article
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Tsybeskov, L., MRS Bulletin 4, 33 (1998).Google Scholar
2. Carosella, C.A., Schiestel, S., Stroud, R.M., Grabowski, K.S., Kendziora, C. and Stoiber, M., Nucl. Instr. Meth. Phys. Res. B 148, 975 (1999).Google Scholar
3. Hubler, G.K., Cotell, C.M., Carosella, C.A. and Schiestel, S., Mat. Sci. Eng. A 253, 212 (1998).Google Scholar
4.SRIM-2000.10, Ziegler, J.F. and Biersack, J.P., IBM Corp. (1998).Google Scholar
5. Taylor, A., X-ray Metallography, Wiley, New York, (1961).Google Scholar
6. Qadri, S.B., Yang, J.P., Skeleton, E.F. and Ratna, B.R., Appl. Phys. Lett. 70 (8), 1020 (1997).Google Scholar
7. Wang, Y. and Herron, N., Phys. Rev. B 42, 7253, (1990)Google Scholar
8. Ila, D., Wu, Z., Smith, C.C., Poker, D.B., Hensley, D.K., Klatt, C. and Kalbitzer, S., Nucl. Instr. Meth. Phys. Res. B 127/128, 570 (1997).Google Scholar
9. Quinten, M., Heilman, A. and Kiesow, A., Appl. Phys. B 68, 707 (1999).Google Scholar
10. Gotschy, W., Vonmetz, K., Leitner, A. and Aussenegg, F.R., Appl. Phys. B 63, 381 (1996).Google Scholar