Comparison of the Quench Rates Attained in Gas Atomized Powders and Melt-Spun Ribbons of Co and Ni Base Superalloys : Influence on Resulting Microstructures

Published online by Cambridge University Press:  15 February 2011

F. Duflos  and
J.F. Stohr
F. Duflos
Affiliation:
Office National d'Etudes et de Recherches Aérospatiales (ONERA) 92320 Chatillon (France)
J.F. Stohr
Affiliation:
Office National d'Etudes et de Recherches Aérospatiales (ONERA) 92320 Chatillon (France)
Get access

Abstract

The cooling rates during solidification of gas atomized Stellite 6 (S6) powders range from 103 K/s to 106 K/s for 400μm to 10 μm diameter powder particles respectively. The microstructures vary from equiaxed type in the coarser particles to fully dendritic, cellular and microcrystalline in the finer particles. In the case of melt spun ribbons, the variations in freezing rate along a cross section of the ribbon produce a change in the microstructure from microcrystalline at cooling rates greater than 107 K/s to cellular and finally dendritic at rates on the order of 106 K/s.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 8 , 1981 , 167
Copyright
Copyright © Materials Research Society 1982

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1]Field, R.D. and Fraser, H.L., Conf. Rapid Solidifn Processing, Reston, Va, Nov 1977, eds Mehrabian, R., Kear, B.H., Cohen, M., p. 270, Baton rouge : Claytors Publ. Divn.Google Scholar
[2]Davies, H.A., Shohoji, N.S., and Warrington, D.H., Conf. Rapid Solidifn. Processing, Reston Va, March 1980, eds Mehrabian, R., Kear, B.H., Cohen, M., p. 153, Baton rouge : Claytors Publ. Divn.Google Scholar
[3]Duflos, F. and Stohr, J.F., to be published in Jal of Material Science.Google Scholar
[4]Glickstein, M.R., R.J. Patterson II Shockley, ibid (Ref. 1), p. 46.Google Scholar
[5]Mehrabian, R., ibid (Ref. 1), p. 9.Google Scholar
[6]Flemings, M.C., Conf. Solidification and Casting of Metals, Sheffield, U.K., July 1977, Published by Metal Society in 1979, London, p. 479.Google Scholar